Invertase-nanogold clusters decorated plant membranes for fluorescence-based sucrose sensor

Abstract

In the present study, invertase-mediated nanogold clusters were synthesized on onion membranes, and their application for sucrose biosensor fabrication was investigated. Transmission electron microscopy revealed free nanoparticles of various sizes (diameter ~5 to 50 nm) along with clusters of nanogold (~95 to 200 nm) on the surface of inner epidermal membranes of onions (Allium cepa L.). Most of the polydispersed nanoparticles were spherical, although some were square shaped, triangular, hexagonal or rod-shaped. Ultraviolet–visible spectrophotometric observations showed the characteristic peak for nanoparticles decorated invertase-onion membrane at approximately 301 nm. When excited at 320 nm in the presence of sucrose, the membranes exhibited a photoemission peak at 348 nm. The fluorescence lifetime of this nanogold modified onion membrane was 6.20 ns, compared to 2.47 ns for invertase-onion membrane without nanogold. Therefore, a sucrose detection scheme comprised of an invertase/nanogold decorated onion membrane was successfully developed. This fluorescent nanogold-embedded onion membrane drop-test sensor exhibited wide acidic to neutral working pH range (4.0-7.0) with a response time 30 seconds (<1 min). The fabricated quenching-based probe had a low detection limit (2x10−9 M) with a linear dynamic range of 2.25x10−9 to 4.25x10−8 M for sensing sucrose. A microplate designed with an enzyme-nanomaterial-based sensor platform exhibited a high compliance, with acceptable percentage error for the detection of sucrose in green tea samples in comparison to a traditional method. With some further, modifications, this fabricated enzyme-nanogold onion membrane sensor probe could be used to estimate glucose concentrations for a variety of analytical samples.

Synthesis and characterization of invertase assisted nanogold clusters on onion membranes and their application for fluorescence-based sucrose sensor.

Introduction

Metal nanoparticles are outstanding building blocks for fabrication of biosensors, due to their surface plasmon resonance shifts in response to a biorecognition event. Properties of nanoparticles vary in accordance with their size and composition, which facilitates diverse applications in various areas including catalysis, sensors and medicine. Production of nanoparticles can be achieved through chemical, physical or biological methods. Among them, there has been considerable attention focused on biological methods for synthesis of metallic nanoparticles, as there is a vast array of biological resources available in nature [1,2]. Furthermore, the biological approach to nanoparticles synthesis is also a low cost, non-toxic, biocompatible and environmentally friendly process.

Enzymes can work as nanoreactors that allow generation of nanostructures often of controlled size by limiting the rate of nucleation of nascent nanocrystals [3]. For example, enzyme-guided nanoparticles have been used for fabrication of biosensors that can detect prostate-specific antigen (a biomarker of prostate cancer), with outstanding sensitivity. The development of optical sensors using enzyme-stimulated synthesis of metallic nanoparticles has been also reported by Willner et al. [4]. According to their study, in the presence of bovine serum albumin, bacterial protease not only mediated biosynthesis of gold (Au) nanoparticles, but also acted as reducing and shape-directing agents. In vitro enzymatic synthesis of Au nanoparticles using alpha-NADPH-dependent sulfite reductase and phytochelatin was reported by Kumar et al. [5]. Kalishwaralal et al., investigated biosynthesis of gold, silver, and gold-silver alloy nanoparticles by harnessing free and exposed thiol groups of α-amylase [1]. Furthermore, the native reducing properties of plant proteins have also been harnessed for synthesis of Au nanoclusters [6,7]. Mittal et al., has reviewed the methods for making nanoparticles using plant extracts and the potential applications of these nanoparticles for various applications [8]. Moreover, the biosynthesis of Au nanoparticles by many plants such as Medicago sativa [9], Azadirachta indica [10], Aloe vera [11], Cinnamomum camphora [12], Magnolia kobus, Diopyros kaki [13], Szyygium aromaticum [14], Putranjiva Roxburghii [15], Cassia auriculata [16], among others, has been well documented.

Consumption of sugar added beverages and numerous other foods have increased across the globe. Therefore, quantitative determination of sugar content in food is an important issue. In particular, there is need for a fast, simple, and reproducible method for determination of sucrose content [17]. Fluorescent-sensing systems have become increasingly popular, due to their versatility, ease of use and low cost. Several analytical techniques have been developed, to exploit changes in fluorescence properties of a molecule in different environments, including quenching, Forster resonance energy transfer, and surface-modified fluorescence (FL) [18]. Invertase (INV; β-fructofuranosidase) is an enzyme with a high rate of enzymatic turnover. Under ambient conditions, nanomolar levels of INV are capable of converting a millimolar concentration of sucrose into glucose, making it an ideal catalyst for amplification of ‘turn-on’ signals in sucrose sensors [19]. Consequently, optical nanoprobe utilizing electrospun polyamide meshes containing gold salts and invertase have been reported to be useful for sugar-sensing [20]. Blue and pink colorimetric assays based on sugar and glucose oxidase-assisted synthesis of nanoparticles for sugar detection, have also been reported [17]. However, reports of fluorometric biosensors for sucrose estimation are very few.

The inner epidermal membrane of the onion bulk scales is a good bio-platform to immobilize enzymes, as it has excellent gas and water permeability for substrates and products. Onion membranes (Oms) mainly consist of elongated tubular cells, with blunt or tapered ends, along with numerous guard cells. For biosensors fabrication, this natural membrane is mechanically stronger than other natural membranes, due to its microfibrillar cellulosic elongated tubular structure. Thus, it could be ideal as a biocompatible platform for enzyme immobilization [21,22]. Kumar and Pundir reported immobilization of lipase on onion membrane and its possible commercial application in food-processing industries [23]. A glucose biosensor comprising glucose oxidase/O-(2-hydroxyl) propyl-3-trimethylammonium chitosan chloride nanoparticle-immobilized on the inner membrane of onion and a dissolved oxygen sensor have also been reported [24]. Furthermore, a glucose biosensor based on onion primary cuticula that immobilized glucose oxidase was reported for determining glucose concentrations in human serum [25].

The objective of our study was to synthesis and characterize invertase-nanogold clusters (INV-NAuCs) embedded in plant membranes and investigate their application in designing fluorescent probes for sucrose detection. The novel feature of our proposed method is employment of a new biomaterial along with enzyme for gold nanomaterial synthesis and biosensor development. Various factors that might influence the sensor performance have been investigated. The fabricated drop-test sensor was then used to detect sucrose in various green tea samples to demonstrate its high sensitivity and specificity.

Results and discussion

Invertase- mediated nanogold synthesis: UV-Visible studies

The UV-Visible absorption spectra of invertase, blank (untreated with invertase) onion membrane, hydrogen tetrachloroaurate (HAuCl4) solution and lastly, onion membrane with invertase and HAuCl4 for 96 h in acetate buffer (20 mM, pH 5.0) are shown in Figure 1a. The HAuCl4 solution had no obvious absorption peak, whereas the spectrum of INV had an absorption peak at 260 nm and blank onion membrane in assay buffer had an absorption peak at 275 nm. After incubating the onion membrane with invertase and gold chloride solution for 96 h, the absorption peak shifted from 275 to 301 nm, which indicated that there was a direct reaction among gold chloride, invertase and onion membrane to form nanogold clusters (NAuCs). Moreover, one minor peak was observed at 540 nm, which is also a characteristic of gold nanoparticles (AuNPs).

Figure 1
figure 1

UV-Visible absorption spectra of invertase-onion membranes. (a) UV-Visible absorption spectra of invertase, blank onion membrane, AuCl4 solution and onion membrane with INV and AuCl4 incubated for 96 h in 20 mM acetate buffer solution (pH 5.0). (b) Periodical UV-visible absorption spectra of invertase-onion membrane with dispersed nanogold in 20 mM acetate buffer solution (pH 5.0). Inset I: Absorption peak at 301 nm; Inset II: Absorption peak at 540 nm. (c) Plot of time versus absorption of nanogold clusters synthesized on an invertase-onion membrane at 301 nm (a) and 540 nm (b), respectively.

Formation of gold nanomaterials was further confirmed by UV–vis spectroscopy. Periodic UV–vis absorption spectra of onion membranes embedded with invertase-nanogold clusters (INV-NAuCs-Om) are shown in Figure 1b. All of spectra displayed the same plasmonic band for major dominant peak I at 301 nm (inset I) and minor surface plasmon peak II at 540 nm (Inset II), which intensified with time. The nanogold biosynthesis process was monitored continuously for 96 h. Absorption intensity increased with duration of incubation, reaching a plateau at 72 h, indicating saturation of nanogold formation on onion membrane after 72 h (Figure 1c). These results are similar to those reported by Parida et al. [6]. Biological activity of INV after nanogold formation was confirmed by DNSA method [26-30].

Nanogold synthesis on the invertase-immobilized onion membrane was consistent with the properties of onion membrane as a reducing and stabilizing agent. A similar approach was used for synthesis of silver nanoparticles, with onion (Allium cepa) extract acting as both a reducing as well as capping agent [31]. Parida et al., stated that reduction of gold nanoparticles occurred in onion extract due to the presence of ample vitamin C, citric acid, ascorbic acid, flavonoids and extracellular electron shutters, etc. [6,32]. However, the specific role of the invertase in the synthesis of nanogold has not been well established. One hypothesis is that a high content of vitamin C, flavonoids, thiosulphonates and other organosulfur in onion membranes are directly involved in the gold reduction mechanism. The exposed S–H groups of invertase may allow enzyme binding to the gold ions via gold–S bond without jeopardizing INV structure. The increased rate of NAuC production by the enzyme indicated a rapid reduction of Au3+ to Au0 by the exposed functional groups of reducing amino acids (e.g. the thiol group of cysteine and the tertiary amine group of histamine) [33]. Furthermore, it is possible that intrinsic enzymatic generation of reactive sulfur species develops surface plasmon resonance at gold nanostructures which may turn them into tiny fluorophores. A more in-depth investigate is needed to understand the internal mechanism responsible for the formation of nanoparticles or clusters in the presence of invertase.

Topological investigation of nanogold membrane

We also analyzed the topography of nanogold using both scanning and transmission electron microscopy (SEM and TEM, respectively). In the SEM images nanoclusters were found aligned with onion epidermal cell walls (Figure 2a-d). The biosynthesized nanogold clusters, ranging in size from 95 to 200 nm, either adhered to or embedded in the membrane. Most of the poly-dispersed nanoparticles were spherical, although other shapes were also visible, e.g. square-shaped, triangular, rectangular, hexagonal and cylindrical, but to a lesser extent. Based on transmission electron microscopy (TEM), these nanoparticles were ~5 to 50 nm in size (Figure 2e). Three-dimensional atomic force microscopic (AFM) images of onion membrane also showed prominent domain impressions of gold nanoclusters into the membrane surface of the onion (Figure 2f).

Figure 2
figure 2

Microscopic images of enzyme-nanogold clusters-onion membrane. SEM images of INV-nanogold onion membrane at various magnifications (a-d); TEM images of various shapes of individual nanoparticles present in nanogold clusters (e) and AFM topography of onion membrane showing gold clusters domains (f).

Characteristic fluorescence spectra of INV- NAuCs- Om

Invertase-onion membranes, both with and without nanoparticles, were excited at 320 nm and the spectra were recorded in an emission range of 330 to 700 nm. The image of INV-Om, indicate that the inner epidermal onion membranes with invertase only did not possess fluorescence, whereas onion membrane decorated with gold clusters did have a fluorescent image (Figure 3a). Furthermore, invertase-immobilized onion membrane had a small peak at 337 nm (Figure 3b). Similarly, Hou et al., reported that the free invertase had an emission peak at 335 nm when excited at the same wavelength [34]. The slight red shift in emission peak (~2 nm) may have been due to the immobilization process. The possibility of emissions arising from the reagents (e.g. HAuCl4, sucrose and the mixture of HAuCl4–sucrose), were also examined. Blank onion membranes incubated with reagents showed very weak fluorescence which was similar to that of the background signal. However, INV-NAuCs-Oms in 25 μL acetate buffer (20 mM, pH 5.0) had a photoemission peak at 346 nm. Perhaps the native reducing property of invertase was also harnessed for synthesis, capping and aggregation of gold particles into stable nanogold clusters. The electrostatic bonding and steric protection due to the bulkiness of the protein may also be responsible for stable INV-Om-scaffolds. Similar observations were reported for photoluminescent BSA-protected nanoparticles, with excitation and emission maxima at 320 and 404 nm, respectively [35].

Figure 3
figure 3

Fluorescence studies of INV-Om and INV-NAuCs-Om. (a) Fluorescence images of INV-OM and INV-NAuCs-Om (b) Fluorescence spectra of INV-Om and INV-NAuCs-Om at excitation wavelength 320 nm.

Fluorescence lifetime and quantum yield of the membrane

The fluorescence lifetime for INV-NAuCs-Om was 6.20 ns and x 2 = 1.150 (Figure 4). In addition, the lifetime for blank Om and INV-Om without nanogold, were 1.23 and 2.47 ns respectively. Therefore, the association of invertase and other proteins with nanoparticles could increase the fluorescence lifetime. The fluorescence average lifetime of INV-nanogold-onion membranes was similar to bovine serum albumin modified gold nanoparticles (BSA-GNPs) previously reported [36].

Figure 4
figure 4

Fluorescence lifetime for INV-NAuCs-Om in aqueous assay buffer solution (yellow line) whereas pink line corresponds to the non-linear least square fit value (x 2 = 1.150). Blue line represents IR spectrum. The lower panel represents the residual plot of the fit.

The quantum yield of gold nanoparticles was conservatively estimated to be 0.065 ± 0.0050 (P = 0.90), approximately eight orders of magnitude greater than that of gold films. Based on the INV-AuNPs-Om high quantum yield (Φ = 0.17 ± 0.004), we may inferred that the membrane is a useful element for fluorescent sensors. In addition, as the invertase-conjugated nano gold particles individually acted as embedded fluorophores in the membranes, it can be concluded that the intrinsic fluorescence of invertase tryptophan was scarcely used. Furthermore, the conservatively estimated quantum yield of INV-gold nanoparticles was found to be approximately seven and twelve orders of magnitude greater than that of blank INV-Om and blank Om, respectively.

Influence of pH on nanogold clusters synthesis and fluorescence property

The influence of pH on the synthesis of nanogold clusters and their morphological properties was studied and observations are provided in Additional file 1 (S1.1 section). The fluorescence of the INV-NAuCs-onion membranes at various pH levels was also checked. For this purpose, membranes in respective pH solutions were excited in the range of 340 to 360 nm and pH range of 3.0 to 11.0. There were emission peaks at 344, 346 and 348 nm for pH 3.0, 4.0 and 5.0, respectively (Additional file 1: Figure S3), whereas emission peaks for pH 6.0 to 9.0 were all observed at 348 nm. For pH 10.0 and 11.0 the fluorescence peaks were observed at 350 and 353 nm, respectively (Additional file 1: Figure S3 inset). The fluorescence intensity from pH 3.0 to 5.0 increased in a linear fashion, with the maxima at pH 5.0, which could be attributed to the invertase pH optima. Nanogold decorated onion membranes were non-fluorescent when they were excited in the range of 540–600 nm.

Effect of invertase and HAuCl4 concentration on nanogold clusters synthesis

The influence of enzyme concentration on nanogold formation and fluorescence intensity is shown and discussed in Additional file 1: Figure S1.2. The chloroauric acid concentration affected the size of nanogold and assemblies formation. For the concentration of HAuCl4 from 0.25 to 1.0 mM, fluorescent gold nanoparticles were formed, with diameters from 2-50 nm (Table 1). As the concentration increased to 1.5 mM, nanoparticles approaching 70 nm (± 32%) in diameter were produced. At 2.0 mM HAuCl4, spherical gold particles (diameter ~90 nm) were formed. These gold nanoparticles had surface plasmon ~543 nm without fluorescence properties. However, further increasing the concentration above 2.0 mM had no major effect on particle growth. The surface plasmon band in the gold nanoparticles solution remained close to 543 nm throughout the reaction period. Therefore, we inferred that nanoparticles were dispersed in the aqueous solution, leaving no evidence of aggregation in UV-Vis absorption spectrum. However, at a high gold salt concentration, steric hindrance and salt crowding on the enzyme surface may change protein structure, eventually causing enzyme precipitation with diminished invertase activity. Surface plasmon resonance peaks and fluorescence intensities with respect to gold salt concentration are shown in Table 1. These results were in good agreement with a previous report, in which effects of gold nanoparticle morphology on adsorbed protein structure and function were thoroughly studied [37].

Table 1 Effect of gold concentration on nanogold formation and fluorescence intensity

Application of the INV-NAuCs-Om sensor for sucrose sensing

Fluorescence measurement allows direct background subtraction strategy while colorimetric assays suffer background interference problem when onion membranes were used directly. Moreover, FL technique is extremely sensitive and fast. FL measurements also provide structure and micro-environment of molecules which help to understand the detailed reaction mechanism. All these special features are important for sensing applications and therefore fluorescent sensors are more attractive as compare to colorimetric sensor.

A schematic representation of the sucrose sensing mechanism behind a microplate sensor modified with a nanoparticle-decorated invertase-onion membrane is shown in Figure 5a. The sucrose-sensing performance of INV-NAuCs-Om was evaluated with fluorometric measurements, which showed a slight blue shift (emission at 348 nm) after sucrose addition at excitation wavelength 320 nm. Furthermore, sucrose was a strong quencher for INV-NAuCs in the UV region. A similar quenching effect was reported by many researchers measuring monosaccharides; therefore, this property is exploited for analyte sensing [38,39]. Consequently, this enzyme-based onion membrane assembly was used as a fluorescence-based optical biosensor. The fluorescence behavior of the biosensor membrane was recorded at room temperature and λex = 320 nm wavelength excitation. Fluorescence intensities of the biosensor membrane steadily decreased with increased sucrose concentrations, with no effect on spectral position and shape. In the present study, glucose, the product of sucrose hydrolysis, not only acted as a quencher, but also as a reducing agent for gold produced in the vicinity of nano gold clusters [39-41]. The same principle was used by Scampicchio et al., where the reaction of glucose (produced by an invertase) with gold salt in alkaline media was used for sucrose sensing [42]. Sensor output was expressed by the change in fluorescence intensity relative to the sucrose concentration (ΔFL/ΔSuc) [39]. The quenching reaction progress was observed for 5 min after sucrose addition for this sensor. However, a typical fast quenching response due to invertase action was observed, within 30 seconds (less than1 min) as shown in Figure 5b. Therefore, the response time for the current sensor was superior to previously reported absorbance-based sucrose sensors [28,43,44]. An additional advantage to note is that these fluorescent biosensor membranes retained invertase activity for one week when stored at 4°C in acetate buffer.

Figure 5
figure 5

Fluorescent properties of INV-NAuCs-Om. (a) Schematic representation of a fluorescent sucrose-sensing mechanism using nanoparticles decorated invertase-onion membrane modified microplate sensor. (b) Quenching signal response of sucrose on INV-NAuCs-Om. (c) Fluorescence spectra of Au-Particles-INV-onion membrane in presence of various concentrations of sucrose (0.2x10−8 to 4.25x10−8 M). Inset I: FL intensity as function of Sucrose concentration. Inset II: Calibration plot using ΔFL vs. sucrose concentration (0.2x10−8 to 4.25x10−8 M).

The linear dynamic range for a sucrose standard obtained was 2.25×10−9 to 4.25×10−8 M, and the limit of detection was 2×10−9 M (Figure 5c). The R2 value was 0.952 which indicates a strong positive relationship of the calibration. Sucrose concentrations < 2×10−9 M were not differentiated from the reference spectrum. Therefore, this was designated as a cut-off value and limit of detection. This threshold was attributed to the limited amount of invertase-nanogold conjugates that can react with sucrose in an onion membrane. The presently designed microplate readout sensor is found to be faster with less sample volume compared to other transducer-based biosensors [28,43-45]. Table 2 summarizes the sensor analysis times, dynamic range and sensitivities of the various sucrose biosensors reported previously.

Table 2 Comparison of the sensor readout time, dynamic range and limit of detection for different types of sucrose biosensors

Spiked samples testing

The feasibility of a quenching biosensor for sucrose detection was evaluated by analysis of green tea samples. Measurements with the fluorescence biosensor were further validated against a standard analytical dinitrosalicylic (DNSA) method. Green tea samples spiked with various sucrose concentrations were prepared for testing, while for blank correction for fluorescence spectra, green tea without sucrose was used. Samples were analyzed using the current biosensor at room temperature (after appropriate dilutions). The comparison of testing results between INV-NAuCs-Om biosensor and DNSA analysis of the sucrose-spiked samples are shown (Table 3). These two methods showed a high compliance, with an acceptable error. Satisfactory recoveries ranging from 94 to 108% were obtained, indicating acceptable accuracy of the proposed detection sensor for sucrose in green tea samples.

Table 3 Spike sample testing with a fabricated INV-NGC-Om sensor

Conclusion

Our present work is apparently the first to use a fluorometric optical onion membrane-based sensor for detection of sucrose. The sensor was based on formation of invertase-induced nanogold clusters and particles within the membrane. Sucrose was hydrolysed by invertase to glucose, which in turn quenched fluorescence. The microplate-based biosensor yielded comparable results with a traditional method for quantifying sucrose in green tea, providing evidence of reliable sensitivity. Therefore, the proposed fluorescent biosensor has potential as a sensitive one-step measurement of sucrose. Furthermore, after some modifications and future investigations, we expect that this technology can be used to estimate glucose concentrations in various sugar-sweetened beverages and other food products. Likewise, this application can be easily adapted in pharmaceutical research where routine screening of glucose is mandatory.

Methods

Materials

Invertase from baker’s yeast (Saccharomyces cerevisiae; EC 3.2.1.26) was purchased from Fluka (Milwaukee, WI, USA). Albumin from bovine serum, glutaraldehyde, sucrose, hydrogen tetrachloroaurate, trisodium citrate, gold chloride and glucose were purchased from Sigma-Aldrich (St. Louis, MO, USA). Ultra-pure water filtered by Millipore SAS 67120, Molsheim, France, was used for all experiments. All other chemicals were of the highest purity and used without further purification.

Invertase assay and immobilization

Large yellow onion bulb (Allium cepa L.) with significantly high natural organosulfur compounds which are also flavor precursors of onion were used for the present study. Fully mature onions were purchased from a local vegetable market (Taipei, Taiwan). The onions were cut into halves, bulb scales separated and inner epidermis was stripped from the outer fleshy scales [22]. This thin bulb epidermal cell wall was used as support for invertase immobilization and matrix for nano gold synthesis. The onion membranes (diameter, 6.0 mm) were thoroughly washed and then incubated with glutaraldehyde (0.01%) in acetate buffer (pH 4.5) at 4°C in the dark, for 1 h. Activated membranes were washed gently three times to remove excess glutaraldehyde and treated with a mixture of invertase (500 μL, 220 U mL−1) and bovine serum albumin (1 mL, 1 mg mL−1) at 4°C for 12 h under gentle stirring. The onion membranes with immobilized invertase were washed twice and tested for enzyme activity using the DNSA method with sucrose (2.5×10−8 M) as substrate [26-28]. Invertase-immobilized onion membranes were then stored at 4°C until use. One unit of invertase activity was defined as the amount of enzyme that hydrolyzed 1 μmole of sucrose in 1 min at 30°C in sodium acetate buffer (20 mM, pH 4.5).

Invertase-mediated nano gold synthesis

Invertase-immobilized onion membranes were immersed in a mixture of 1.0 mL hydrogen tetrachloroaurate (0.5 mM) and 1.0 mL of assay buffer for 24 h at 55°C in a shaking incubator. The transparent, thin onion membranes changed from colorless to a slight yellowish pink color, indicating nanogold synthesis during incubation. Resulting membranes were stored at 4°C in acetate buffer (pH 5.0).

UV–vis absorbance spectroscopy

UV-Visible spectra analysis was used to confirm reduction of hydrogen tetrachloroaurate (HAuCl4) and formation of nanogold on the invertase-bound onion membranes. Biosynthesis of invertase-assisted nanogold clusters and nanoparticles on the Oms were monitored periodically for 72 h. The Om samples were scanned from 300 to 600 nm wavelengths using a dual beam UV-Visible spectrophotometer (1 nm resolution). The UV–vis spectra of the immobilized membranes in assay buffer solution was measured and compared to blank onion membranes.

Fluorescent imaging

The invertase-immobilized onion membranes (1.0 × 1.0 cm2) both with and without nanogold were analyzed under fluorescence imaging using a Leica MZ16F fluorescence stereomicroscope equipped with a DFC 500 camera having GFP filter from Leica Microsystems (Switzerland) Ltd. A magnification range 7.1× to 115×, with a 10× eyepiece, was used to obtain optical images (exposure time of 10.41 s and gain of 80.4%). Images were analyzed with Leica image manager 50, V1.20 software.

SEM images of the onion membrane

A scanning electron microscope (Model JEOL JSM-6300 F, Tokyo, Japan; 2–5 kV with Auto Fine Coater, JEOL-JFC-1600E Ion Sputtering Device) was used to study modified invertase-onion membranes. During SEM analysis, onion membrane(s) were mounted on stubs and coated with Au/Pd. SEM micrographs of both the invertase immobilized and those that were blank were taken at various magnifications.

TEM study of onion membrane

The invertase-onion membranes with nanogold clusters were also analyzed by transmission electron microscopy to identify the effects of pH on nanogold synthesis. The INV-NAuCs-Om was cut into circles (~ Φ3 mm) using a razor at room temperature. Membrane pieces were supported on a conventional Φ3 mm Cu mesh with a carbon micro-grid. The TEM observations were performed using a JEOL JEM-3000 F transmission electron microscope (Topcon Co., Ltd., Japan) operated at an accelerating voltage of 300 kV.

Fluorescence lifetime of INV-NAuCs-Om

Fluorescence lifetime data for light-emitting NAuCs-onion membranes were obtained with an FLS920 combined steady-state lifetime fluorescence spectrometer (Hitachi, Japan). Decay curves were analyzed with a multi-exponential iterative fitting program provided with the instrument. The quantum yield (QY) of INV-NAuCs-Om and INV-Om were determined using l-tryptophan as a criterion (QY = 0.14) at room temperature.

Sensor fabrication and sucrose measurement

To develop a simple read-out and highly sensitive biosensor system, we used a 96-well fluorescence-compatible microplate as a convenient platform. There are many reports of innovative optical and electrochemical biosensors using a microplate as a reusable component of biosensor [22,29,30]. Black polystyrene FluoroNunc™/LumiNunc™ plates (with minimum back-scattered light and background fluorescence) were used for the measurements. Tecan Infinite® 200 PRO microplate reader with Tecan i-control software was used for microplate analysis. The INV-NAuCs-Om disc (Φ 5 mm) was prepared and adhered on a cover glass disc, without any adhesive, with the hydrophobic side of the onion membrane downward. These modified glass sensor chips were placed at the bottom of each well of the microplate cassette. The INV-NAuCs-Om microplate sensor was calibrated using a standard sucrose solution and fluorescence measurements were recorded. After sensor characterization, sucrose-spiked real samples were also tested. An INV-NAuCs-Om modified microplate was used as a transducer tool to evaluate performance of bioconjugated membranes. For this, 25 μL buffered sucrose solution (2.5×10−8 M) was added to the sensing zone and fluorescence was analyzed by exciting the probe at 320 nm. Thereafter, sucrose concentration was increased to 4.25×10−8 M, and fluorescence intensity at 348 nm of the INV-NAuCs-Om sensor was measured. Experiments were repeated at least three times, and similar results were obtained. One representative set of data was used for analysis as described.

Preparation and determination of sucrose in spiked samples

Spike recovery is important to investigate the accuracy of an analytical method. The applicability of the fabricated sensor was evaluated using green tea samples obtained from a local market (Taipei, Taiwan). Tea samples were filtered through a 0.22 μm membrane prior to dilution with assay buffer (acetate buffer, 20 mM, pH 5.0). Spiked tea samples were prepared with 25–150 ng mL−1 sucrose concentrations. For testing, 25 μL buffered spiked sample solution was drop-tested on the sensor zone and fluorescence analysis was performed by exciting the INV-NAuCs-Om probe at 320 nm. The quenched fluorescence signal was monitored for all tea samples.

Abbreviations

INV:

Invertase

Om:

Onion membrane

AuNPs:

Gold nanoparticles

NAuCs:

Nanogold clusters

DNSA:

Dinitrosalisilic acid

TEM:

Transmission electron microscopy

SEM:

Scanning Electron Microscopy

AFM:

Atomic force microscopy

FL:

Fluorescence

References

  1. Kalishwaralal K, Gopalram S, Vaidyanathan R, Deepak V, Pandian SRK, Gurunathan S. Optimization of α-amylase production for the green synthesis of gold nanoparticles. Colloids Surf B Biointerfaces. 2010;77:174–80.

    Article  CAS  Google Scholar 

  2. Thakkar NK, Mhatre SS, Parikh RY. Biological synthesis of metallic nanoparticles. Nanomed Nanotechnol Biol Med. 2010;6:257–62.

    Article  CAS  Google Scholar 

  3. Rodríguez-Lorenzo L, Rica R, Álvarez-Puebla RA, Liz-Marzán LM, Stevens MM. Ultrasensitive detection of PSA in serum. Nature Mater. 2012;11:604–7.

    Article  Google Scholar 

  4. Willner I, Baron R, Willner B. Growing metal nanoparticles by enzymes. Adv Mater. 2006;18:1109–20.

    Article  CAS  Google Scholar 

  5. Kumar SA, Abyaneh MK, Gosavi SW, Ahmad A, Khan MI. Sulfite reductase-mediated synthesis of gold nanoparticles capped with phytochelatin. Biotechnol Appl Biochem. 2007;47:191–5.

    Article  CAS  Google Scholar 

  6. Parida UK, Bindhani BK, Nayak P. Plant extract mediated synthesis of silver and gold nanoparticles and its antibacterial activity against clinically isolated pathogens. World J Nanosci Eng. 2011;1:93–8.

    Article  CAS  Google Scholar 

  7. MubarakAli D, Thajuddin N, Jeganathan K, Gunasekaran M. Plant extract mediated synthesis of silver and gold nanoparticles and its antibacterial activity against clinically isolated pathogens. Colloids Surf B Biointerfaces. 2011;85:360–5.

    Article  CAS  Google Scholar 

  8. Mittal AM, Chisti Y, Banerjee UM. Synthesis of metallic nanoparticles using plant extracts. Biotechnol Adv. 2013;31:346–56.

    Article  CAS  Google Scholar 

  9. Gardea-Torresdey JL, Parsons JG, Gomez E, Peralta-Videa J, Troiani HE, Santiago P. Formation and growth of Au nanoparticles inside live alfalfa plants. Nano Lett. 2002;2:397–401.

    Article  CAS  Google Scholar 

  10. Shankar SS, Rai A, Ankamwar B, Singh A, Ahmad A, Sastry M. Biological synthesis of triangular gold nanoprisms. Nature Mater. 2004;3:482–8.

    Article  CAS  Google Scholar 

  11. Chandran PA, Chaudhary M, Pasricha R, Ahmad A, Sastry M. Synthesis of gold nanotriangles and silver nanoparticles using Aloe vera plant extract. Biotechnol Prog. 2006;22:577–83.

    Article  CAS  Google Scholar 

  12. Huang J, Li Q, Sun D, Lu Y, Su Y, Yang X, et al. Biosynthesis of silver and gold nanoparticles by novel sundried cinnamomum camphora leaf. Nanotechnol. 2007;18:105104–11.

    Article  Google Scholar 

  13. Song JY, Jang HK, Kim BS. Biological synthesis of gold nanoparticles using Magnolia kobusand Diopyros kaki leaf extracts. Process Biochem. 2009;44:1133–8.

    Article  CAS  Google Scholar 

  14. Singh AK, Talat M, Singh DP, Srivastava ON. Biosynthesis of gold and silver nanoparticles by natural precursor clove and their functionalization with amine group. J Nanopart Res. 2010;12:1667–75.

    Article  CAS  Google Scholar 

  15. Badole MR, Dighe VV. Synthesis of gold nano particles using Putranjiva roxburghii wall leaves extract. Int J Drug Discovery Herbal Res. 2012;44:275–8.

    Google Scholar 

  16. Venkatachalam M, Govindaraju K, Mohamed Sadiq A, Tamilselvan S, Ganesh Kumar V, Singaravelu G. Functionalization of gold nanoparticles as antidiabetic nanomaterial. Spectrochim Acta Mol. 2013;116:331–8.

    Article  CAS  Google Scholar 

  17. Plazzo G, Facchini L, Mallardi A. Colorimetric detection of sugars based on gold nanoparticle formation. Sensors Actu B. 2012;161:366–71.

    Article  Google Scholar 

  18. Simonian AL, Good TA, Wang SS, Wild JR. Nanoparticle-based optical biosensors for the direct detection of organophosphate chemical warfare agents and pesticides. Anal Chim Acta. 2005;534:69–77.

    Article  CAS  Google Scholar 

  19. Xiang Y, Lu Y. Using personal glucose meters and functional DNA sensors to quantify a variety of analytical targets. Nature Chem. 2011;3:697–703.

    Article  CAS  Google Scholar 

  20. Scampicchio M, Fuenmayor CA, Mannino S. Sugar determination via the homogeneous reduction of Au salts: a novel optical measurement. Talanta. 2009;79:211–5.

    Article  CAS  Google Scholar 

  21. Kumar J, D’Souza SF. Inner epidermis of onion bulb scale: as natural support for immobilization of glucose oxidase and its application in dissolved oxygen based biosensor. Biosens Bioelectron. 2009;24:1792–5.

    Article  CAS  Google Scholar 

  22. Kumar J, D’Souza SF. Immobilization of microbial cells on inner epidermis of onion bulb scale for biosensor application. Biosens Bioelectron. 2011;26:4399–404.

    Article  CAS  Google Scholar 

  23. Kumar VR, Pundir CS. Covalent immobilization of lipase onto onion membrane affixed on plastic surface: Kinetic properties and application in milk fat hydrolysis. Indian J Biotechnol. 2007;6:479–84.

    Google Scholar 

  24. Wang F, Yao J, Russel M, Chen H, Chen K, Zhou Y, et al. Development and analytical application of a glucose biosensor based on glucose oxidase/O-(2-hydroxyl)propyl-3-trimethylammonium chitosan chloride nanoparticle-immobilized onion inner epidermis. Biosens Bioelectron. 2010;25:2238–43.

    Article  CAS  Google Scholar 

  25. Jia W, Liu W, Zhang Y, Cui M, Shuang S, Dong C, et al. Determination of glucose in human serum based on an onion primary cuticula biosensor immobilized glucose oxidase. Anal Methods. 2012;4:1432–7.

    Article  CAS  Google Scholar 

  26. Miller GL. Use of dinitrosalicylic acid reagent for determination of reducing sugar. Anal Chem. 1959;31:426–8.

    Article  CAS  Google Scholar 

  27. Bagal DS, Vijayan A, Aiyer RC, Karekar RN, Karve MS. Fabrication of sucrose biosensor based on single mode planar optical waveguide using co-immobilized plant invertase and GOD. Biosens Bioelectron. 2007;22:3072–9.

    Article  CAS  Google Scholar 

  28. Bagal-Kestwal D, Kestwal R, Chiang BH, Karve MS. Development of dip-strip sucrose sensors: application of plant invertase immobilized in chitosan-guar gum, gelatin and poly-acrylamide films. Sensors Actuat B. 2011;160:1026–33.

    Article  CAS  Google Scholar 

  29. Kalyuzhny AE. Protein blotting and detection. Methods Mol Biol. 2009;536:355–65.

    Article  CAS  Google Scholar 

  30. Liu Y, Jia S, Guo LH. Synthesis of chitosan-Prussian blue-graphene composite nanosheets for electrochemical detection of glucose based on pseudobienzyme channeling. Senso Actuators. 2012;161:334–40.

    Article  CAS  Google Scholar 

  31. Saxena A, Tripathi RM, Singh RP. Synthesis of silver nanoparticles using onion (Allium cepa) extract and their antibacterial activity. Dig J Nanomater Bios. 2010;5:427–32.

    Google Scholar 

  32. Pandey S, Oza G, Gupta A, Shah R, Sharon M. Green synthesis of highly stable gold nanoparticles using momordica charantia as nano fabricator. Euro J Exp Bio. 2012;2:475–83.

    CAS  Google Scholar 

  33. Sanghi R, Verma P, Puri S. Enzymatic formation of gold nanoparticles using Phanerochaete Chrysosporium. Adv Chem Engg Sci. 2011;1:154–62.

    Article  CAS  Google Scholar 

  34. Hou Y, Hansen TB, Staby A, Cramer SM. Effect of urea induced protein conformational changes on ion exchange chromatographic behaviour. J Chromatograph. 2010;1217:7393–400.

    Article  CAS  Google Scholar 

  35. Liu L, Zheng HZ, Zhang ZJ, Huang YM, Chen SM, Hu YF. Photoluminescence from water-soluble BSA-protected gold nanoparticles. Spectrochim Acta A. 2008;69:701–5.

    Article  Google Scholar 

  36. Chakraborty S, Joshi P, Shanker V, Ansari ZA, Singh SP, Chakrabarti P. Contrasting effect of gold nanoparticles and nanorods with different surface modifications on the structure and activity of bovine serum albumin. Langmuir. 2011;27:7722–31.

    Article  CAS  Google Scholar 

  37. Gagner JE, Lopeze MD, Dordickb JS, Siegel RW. Effect of gold nanoparticle morphology on adsorbed protein structure and function. Biomaterials. 2011;32:7241–52.

    Article  CAS  Google Scholar 

  38. Panigrahi S, Kundu S, Ghosh SK, Nath S, Pal T. Sugar assisted evolution of mono- and bimetallic nanoparticles. Colloids Surf A Physicochem Eng Aspects. 2005;264:133–8.

    Article  CAS  Google Scholar 

  39. Anker JN, Hall WP, Lyaders O, Shah NC, Zhao J, Van Duyne RP. Biosensing with plasmonic nanosensors. Nat Mater. 2008;7:442–53.

    Article  CAS  Google Scholar 

  40. Huang X, Neretina S, El-Sayed MA. Gold nanorods: from synthesis and properties to biological and biomedical applications. Adv Mater. 2009;21:4880–910.

    Article  CAS  Google Scholar 

  41. Hussain AMP, Sarangi SN, Kesarwani JA, Sahu SN. Au-nanocluster emission based glucose sensing. Biosens Bioelectron. 2011;29:60–5.

    Article  CAS  Google Scholar 

  42. Scampicchio M, Arecchi A, Mannino S. Optical nanoprobes based on gold nanoparticles for sugar sensing. Nanotechnol. 2009;20:135501–10.

    Article  Google Scholar 

  43. Soldatkin OO, Peshkova VM, Dzyadevych SV, Soldatkin AP, Jaffrezic-Renault N, El’skaya AV. Novel sucrose three-enzyme conductometric biosensor. Mater Sci Eng C. 2008;28:959–64.

    Article  CAS  Google Scholar 

  44. Haghighi B, Varma S, Alizadeh SFM, Yigzaw Y, Gorton L. Prussian blue modified glassy carbon electrodes-study on operational stability and its application as a sucrose biosensor. Talanta. 2004;64:3–12.

    Article  CAS  Google Scholar 

  45. Kitova A, Reshetilov A, Ponamoreva O, Leathers T. Microbial biosensors for selective detection of disaccharides. Internet J Microbiol. 2009;8:2.

    Google Scholar 

  46. Antiochia R, Tasca F, Mannina L. Osmium-polymer modified carbon nanotube paste electrode for detection of sucrose and fructose. Mater Sci Appl. 2013;4:15–22.

    CAS  Google Scholar 

Download references

Acknowledgment

The authors gratefully acknowledge all financial assistance from the National Science Council, Taipei, Taiwan (NSC-100-2221-E-002-032) and National Taiwan University (Project No. 101R4000). We also are grateful to Dr. Senthil Kumar and Prof. Kai-Wun Yeh for providing facilities and guidance during this research.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Been-Huang Chiang.

Additional information

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

DK gathered the research data. DK and RK contributed to the project design, data analysis and data interpretation and manuscript preparation. All authors read and approved the final manuscript.

Authors’ information

Dr. Dipali Bagal-Kestwal is Post-Doctoral research fellow, working in the biosensor research for last 12 years. She completed her PhD in enzyme-based biosensors and is currently working on nanomaterial-based biosensors under the guidance of Prof. Been-Huang Chiang. Dr. Rakesh Mohan Kestwal has also been involved in biosensor research for the last 7 years and now he is working on the pesticide biosensors with Prof. Chiang. Professor Been-Huang Chiang is a distinguished Professor at the Institute of Food Science and Technology, National Taiwan University, Taipei, Taiwan, ROC. He is actively engaged in food science and food safety research. His expertise includes food packaging, separation technology, functional foods and fabrication of different enzyme based sensors for food application.

Additional file

Additional file 1:

Invertase-nanogold based quenching sucrose sensor.

Rights and permissions

Open Access  This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.

The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.

To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.

The Creative Commons Public Domain Dedication waiver (https://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Bagal-Kestwal, D., Kestwal, R.M. & Chiang, BH. Invertase-nanogold clusters decorated plant membranes for fluorescence-based sucrose sensor. J Nanobiotechnol 13, 30 (2015). https://doi.org/10.1186/s12951-015-0089-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s12951-015-0089-1

Keywords