Effects of various heavy metal nanoparticles on Enterococcus hirae and Escherichia coli growth and proton-coupled membrane transport

Journal of Nanobiotechnology volume 13, Article number: 69 (2015) Cite this article

Abstract

Background

Due to bacterial resistance to antibiotics there is a need for new antimicrobial agents. In this respect nanoparticles can be used as they have expressed antibacterial activity simultaneously being more reactive compared to their bulk material. The action of zinc (II), titanium (IV), copper (II) and (I) oxides thin films with nanostructured surface and silver nanoscale particles on Enterococcus hirae and Escherichia coli growth and membrane activity was studied by using microbiological, potentiometric and spectrophotometric methods.

Results

It was revealed that sapphire base plates with deposited ZnO, TiO2, CuO and Cu2O nanoparticles had no effects neither on E. hirae nor E. coli growth both on agar plates and in liquid medium. Concentrated Ag nanoparticles colloid solution markedly affected bacterial growth which was expressed by changing growth properties. E. hirae was able to grow only at <1:200 dilutions of Ag nanoparticles while E. coli grew even at 1:10 dilution. At the same time Ag nanoparticles directly affected membranes, as the FOF1-ATPase activity and H+-coupled transport was changed either (E. coli were less susceptible to nanoparticles compared to E. hirae). Ag nanoparticles increased H+ and K+ transport even in the presence of N,N′-dicyclohexylcarbodiimide (DCCD), inhibitor of FOF1. The stoichiometry of DCCD-inhibited ion fluxes was disturbed.

Conclusions

These results point out to distinguishing antibacterial effects of Ag nanoparticles on different bacteria; the difference between effects can be explained by peculiarities in bacterial membrane structure and properties. H+-K+-exchange disturbance by Ag nanoparticles might be involved in antibacterial effects on E. hirae. The role of FOF1 in antibacterial action of Ag nanoparticles was shown using atpD mutant lacked β subunit in F1.

Background

In recent years many researchers have tried to find out new antibacterial agents, as many microorganisms have acquired antibiotic resistance [1]. In general, microorganisms acquire resistance to antibiotics during antibacterial therapy and other application fields and this property becomes inheritable. As a result of that process high-doses of antibiotics are used which are very toxic [2]. Nanoparticles can be used as an alternative to antibiotics as there are a number of advantages [3]. For instance, nanoparticles of metals with the size of 10 nm and less have high reactivity and can react with other substances practically without complementary energy. A share of surface atoms in nanoparticles is considerably greater than in bulk material and increases with reduction of particle size. Chemical bonds of nanoparticles surface atoms are not compensated and it results in appearance of new electrical, chemical, mechanical, toxic and other properties. At the same time the advantages with nanoparticles are their safety and biocompatibility [4].

It is well known that heavy metal ions affect bacterial cells and different mechanisms are proposed for the explanation of such effects. The results obtained in our laboratory suggested that the target for heavy metal ions might be the FOF1-ATPase in bacterial cells which in turn regulated the growth of bacteria [5, 6]. Moreover the action of metal ions can be direct or can be mediated by redox potential [5, 6]. Such effects are known for silver ions too which can be explained by interaction of metal ions with bacterial cell membrane blocking respiration and electron transfer which in turn collapses proton motive force [7]. The antimicrobial activity of Ag nanoparticles can occur as a result of nanoparticles penetration into the bacteria causing damage of cell membrane [8].The effects of ions and nanoparticles of heavy metals can differ among bacteria and further investigation of the mechanisms of nanoparticles action is needed.

Nowadays nanoparticles research is of great interest because they can be used in various fields as medicine, veterinary, food industry, manufacturing and etc. These materials can be used for beneficial purposes while maintaining initial properties and functions [4].

Susceptibility of different microorganisms to nanoparticles depends on various factors. It is known that the influence of nanoparticles on Gram-positive and Gram–negative bacteria is not the same which can be explained by chemical and structural differences in bacterial cell wall [2]. Another factor can be bacterial growth rate. Slow growing bacteria are less susceptible to nanoparticles as the expression of stress-response genes takes place during the bacterial growth [2, 9]. The exact cellular mechanisms for the effects of nanoparticles are not clear yet but the toxicity of different nanoparticles depends on type of nanoparticles as well as on bacterial strains, concentration of bacteria and nanoparticles, pH, temperature etc. It is suggested that the addition of Ag and CuO nanoparticles to Bacillus subtilis growth medium leads to the cell wall damage, disruption of biochemical processes while the nanoparticles of TiO2 have no toxicity on this bacterium in dark conditions. In the case of Pseudomonas aeruginosa TiO2 causes loss of respiratory activity while Ag nanoparticles disturb permeability and cell division [2]. Ag nanoparticles are one of the most promising nanomaterials today as they have high antibacterial activity [10, 11]. The toxicity of Ag depends on size of nanoparticles: small nanoparticles (1–10 nm) are able to pass through bacterial cell wall, while larger nanoparticles not [7, 12, 13]. By attaching to bacterial cell wall Ag nanoparticles change the permeability of membrane and inhibit cell respiration [12–14]. At the same time, these nanoparticles are non-toxic at low concentrations for human cells [15]. There is no clear information about the targets and the mechanisms of the nanostructures and nanoparticles effects on Enterococcus hirae. These bacteria have antibacterial activity (against other bacteria) [16], are used in food industry and could be added as bio-preservatives [17, 18]. They are also used in the production of mixed acids, especially lactic acid [19, 20]. At the same time among enterococci there are pathogenic species which can cause endocarditis, infections of urinary tract and central nervous system [17]. In this respect, it is of significance to study metabolism and behavior of enterococci in the presence of different external factors including heavy metal nanoparticles. Moreover, the effects of nanoparticles can be distinguishing for different bacteria and, therefore, these effects should be further studied and appropriate mechanisms should be revealed.

The aim of this work was to study the action of different materials (such as CuO, TiO2 and ZnO) with nanostructured surface and Ag nanoparticles on Enterococcus hirae and Escherichia coli growth, ATPase activity and proton-coupled ions transport through membrane. It has been shown that the effects were different; they depended on bacterial species and the type of nanoparticles. In addition, it has been determined that the concentrated Ag nanoparticles colloid solution was more effective than TiO2 and ZnO thin films with nanostructured surface and microporous Cu2O tablet with nanoscale roughness of surface. The changes in ion membrane transport and ATPase activity were established.

Results

Effects of TiO2 and ZnO thin films with nanostructured surface and microporous Cu2O tablet with nano-scale roughness of surface on bacteria

The effects of TiO2 and ZnO thin films with nanostructured surface and microporous Cu2O tablet with nanoscale roughness of surface on bacteria were determined on agar plates and in liquid growth medium. It was established that none of nanoparticles had any influence on bacterial growth on agar plates. In the case of neither E. hirae nor E. coli no growth inhibition zones were determined in the presence of all types of nanoparticles. The growth of bacteria was the same as in the case of control sample (clean sapphire substrate without any deposited film). These sapphire substrate had no influence on bacterial growth in liquid growth medium either (no statistically reliable differences were observed compared to control sample, p > 0.05). It was determined that lag phase duration and specific growth rate were the same as in the case of control sample (not shown). These effects did not depend on the volume of growth medium (the effects were studied in different volumes: 15, 10, 5 and 3 ml). No effects were observed even in the case of 3 ml.

Effects of concentrated Ag nanoparticles colloid solution on bacterial growth

The growth of E. coli and E. hirae was determined in the presence of concentrated Ag nanoparticles diluted by 10; 20; 50; 100; 200 and 500 folds. It was interesting to notice that the effects depended on bacterial species. With E. hirae the growth inhibition was stronger as no bacterial growth was detected in the case of 1:10; 1:20; 1:50 and 1:100 dilutions. In the case of 200 and 500 fold dilutions bacteria were able to grow but lag phase duration was prolonged while specific growth rate was decreased (Figs. 1, 2). When concentrated Ag nanoparticles were diluted by 500 fold, the growth was approximately the same as in the control sample (see Figs. 1, 2). The same pattern was observed with the atp mutant MS116 either but in the case of the mutant strain the effects were stronger as bacterial growth was detected only with 500 fold dilution of Ag nanoparticles. In contrast to wild type strain, MS116 was not able to grow when nanoparticles were diluted by 200 fold while with 500 fold dilution lag phase duration and specific growth rate was almost the same as in the control sample (not shown).

Fig. 1
figure 1

The effect of dioctyl sodium sulfosuccinate (DSS) alone and together with Ag nanoparticles on E. hirae ATCC9790 and E. coli K-12 lag phase duration. Control was bacterial growth without nanoparticles. Ag nanoparticles and DSS were diluted by 10, 20, 50, 100, 200 and 500 folds. For details see “Methods”

Full size image
Fig. 2
figure 2

The effect of dioctyl sodium sulfosuccinate (DSS) alone and together with Ag nanoparticles E. hirae ATCC9790 and E. coli K-12 specific growth rate. For details see “Methods”

Full size image

Interestingly, E. coli was able to grow even when concentrated Ag nanoparticles were diluted by tenfold. Lag phase duration was notably prolonged (by ~1.6 fold) while specific growth rate was 2.5- fold lower compared to the control sample (see Figs. 1, 2). These effects had a concentration dependent manner (see Fig. 1). As in the case of E. hirae in the presence of Ag nanoparticles diluted by 500 fold the E. coli growth was almost the same as in the control sample. It is known that dioctyl sodium sulfosuccinate (DSS) has antibacterial activity especially against Gram-positive bacteria due to its ability to increase the permeability of bacterial cell [21]. To exclude the role of DSS in the inhibition of bacterial growth we have examined the effects of DSS solution on bacterial growth within the same concentration range that was present in concentrated Ag nanoparticles colloid solution (see Materials and methods). As it is shown in Figs. 1 and 2, the solution of DSS had influence both on E. hirae and E. coli growth but the effects were lower by 1.5–1.7 fold. Moreover it is suggested that in solution, where Ag nanoparticles and DSS are present, synergistic effects can be observed [21].

Effects of concentrated Ag nanoparticles colloid solution on bacterial proton-coupled membrane transport and ATPase activity

As in the case of E. hirae bacterial growth was detected only in the case of 1:200 and 1:500 dilutions of Ag nanoparticles, proton-coupled membrane transport and ATPase activity was measured in the presence of these concentrations. It was shown (Fig. 3) that in the case of 1:200 dilution the ATPase activity was lowered by 15 fold compared to the control sample. Moreover when 0.1 mM N,N′-dicyclohexylcarbodiimide (DCCD), inhibitor of the FOF1-ATPase, was added into the assay medium no ATPase activity was detected (see Fig. 3). The results indicate that the FOF1-ATPase might be a target for Ag nanoparticles in bacterial membrane. As in the case of growth, Ag nanoparticles diluted by 500 fold had no significant effects on ATPase activity as the values were almost the same, as in the control sample (see Fig. 3). For comparison ATPase activity was determined in the presence of DSS either (see Fig. 3). It was shown that in the absence of 0.1 mM DCCD ATPase activity was detected even in the presence of DSS in the case of 100 fold dilution. The values with 200 fold diluted DSS were higher in comparison to the values with Ag nanoparticles in the same concentration (see Fig. 3). The results confirm data observed during bacterial growth, as the effects of Ag nanoparticles were stronger compared to DSS effects. Similar effects were detected with the atp mutant MS116 too but the effects were expressed in much less extent (not shown).

Fig. 3
figure 3

Changes in ATPase activity of membrane vesicles of E. hirae in the presence of Ag nanoparticles and DSS in K+-containing medium. For details, see “Methods”

Full size image

The presence of nanoparticles in assay medium led to the increase in H+ and K+ fluxes (Table 1). More notable effects were with 200 fold dilution when H+ and K+ fluxes were increased by 2.04 fold and 2.78 fold, respectively (see Table 1). It was revealed that ion fluxes were increased even in the presence of 0.1 mM DCCD, inhibitor of the FOF1-ATPase [22]. In addition, the ratio (stoichiometry) of DCCD-sensitive H+ and K+ fluxes was also determined (see Tables 1, 2) which can be indicative for the specific mechanism of H+–K+ exchange [22, 23]. The ratio was changed depending on concentration of nanoparticles (see Table 1). These results indicate that some disturbance took place after the treatment of bacteria with nanoparticles and the membrane permeability might be changed.

Table 1 Proton and potassium ions fluxes across the membrane of E. hirae ATCC9790 at the presence of Ag nanoparticles and/or 0.1 mM DCCD
Full size table
Table 2 Proton and potassium ions fluxes across the membrane of E. coli K-12 at the presence of Ag nanoparticles and/or 0.1 mM DCCD
Full size table

With E. coli similar effects were detected but with less extent: H+ and K+ fluxes were increased too but the effects were weaker. Ions fluxes were detected even in the case of 1:10, 1:50 and 1:100 dilutions of Ag nanoparticles concentration and in the presence of 0.1 mM DCCD (Table 2). The effects had a concentration dependent manner and the ratio of DCCD-inhibited fluxes was fixed (see Table 2).

Discussion

Nowadays heavy metal nanoparticles are widely used in various fields including medicine and drug production. Nanoparticles are used as drug carriers which allow delivering drugs directly in the therapy of various tumors, such as breast cancer, lung cancer [24]. As nanoparticles have antibacterial activity they are used during wound healing and postoperative recovery. The use of nanoparticles as immunomodulators is also known in the field of clinical medicine [25]. At the same time the exact mechanisms of action and toxicity of nanoparticles are not known yet. In this respect we have tried to determine effects of different nanoparticles on Gram-positive (E. hirae) and Gram-negative (E. coli) bacterial strains and found out possible targets in bacterial cells.

As it was mentioned above, the effects of nanoparticles depend on bacterial species (the effects were stronger with E. hirae) which can be explained by differences in bacterial cell wall structure, composition of membrane and membrane-associated properties [22, 26]. These results are in accordance with data reported recently [2]. It has been shown that Gram-positive strains show higher susceptibility to nanoparticles than Gram-negative strains [27–29]. Yoon and coauthors [27] determined the susceptibility constants and revealed that B. subtilis is more sensitive to Ag nanoparticles compared to E. coli. Similar effects were observed by Azam and coauthors [29]. It was shown that Gram-negative E. coli and P. aeruginosa for both Cu2O and ZnO films with nanostructured surfaces had lower inhibition-zone sizes than Gram-positive B. subtilis and S. aureus [29]. It is also established that the effects of nanoparticles depend on their size, stability and concentration in the growth medium [29]. At the same time the effects depend on type of nanoparticles as it was shown that Ag nanoparticles have stronger bactericidal effect against E. coli and S. aureus compared to Cu nanoparticles [9]. Similar effects have been observed, as Ag nanoparticles had the strongest effects (see Figs. 1, 2). At the same time Ag nanoparticles were in concentrated colloid solution, and the interaction of nanoparticles with bacterial cells was easier compared to ZnO and TiO2 thin films and microporous Cu2O. Moreover separate addition of DSS which was used as a surfactant and stabilizer in Ag nanoparticles colloid solution caused an inhibition in bacterial growth but the effect was lowered by 1.7 fold compared to colloid solution (see Figs. 1, 2). These results indicate the specific action of Ag nanoparticles. The effects of Ag nanoparticles on E. hirae were investigated by Manivasagam et al. [8] using well-diffusion method; the other methods are required. However, differences between the effects on various bacteria should be clarified and mechanisms of action are not known yet.

It is known that Ag has been used in biotechnology and many fields as medicine, veterinary and cosmetics, as a water disinfection agent, in jewelry production as an antimicrobial and antifungal agent [30]. When this metal is prepared as a nanoparticle with sizes of 10–12 nm the antimicrobial effect is better as they have larger specific surface area, as suggested [27]. It is also proposed that Ag nanoparticles are able to interact with bacterial membranes increasing permeability, changing structure of membranes and finally leading to cell death [31]. After penetrating through bacterial membrane Ag nanoparticles are able to damage DNA or inactivate enzymes [32, 33]. As it was determined [1], Ag nanoparticles are more toxic for microorganisms compared to other metals simultaneously they are non-toxic for human cells at low concentrations [34]. We have shown that Ag nanoparticles affect not only the growth of both E. hirae and E. coli (see Figs. 1, 2) but H+ and K+ fluxes were changed in the presence of these nanoparticles (see Tables 1, 2).

It is suggested that membrane-associated ATPase activity of E. coli and E. hirae and H+-coupled K+ transport is the result of the FOF1-ATPase interaction with K+ transport system, Trk and KtrI system, respectively [22, 23, 35, 36]. Ion fluxes increased even in the presence of DCCD were indicating that Ag nanoparticles affect bacterial membrane leading to changes in structure and permeability. These effects depend on bacterial species either. In the case of E. coli the ratio of DCCD-sensitive H+–K+ exchange was fixed (see Table 2) while with E. hirae the stoichiometry was changed indicating that the interaction between the FOF1-ATPase and KtrI system was disturbed (Fig. 4). Such effects can explain the stronger effects with E. hirae compared to E. coli. It was shown that Ag nanoparticles directly affect the FOF1-ATPase as this ATPase activity was changed even in the absence of DCCD and the effects were stronger with wild-type strain. DSS affected ATPase activity either but the values were higher. Ag nanoparticles might affect the interaction of the FOF1-ATPase with secondary transport systems or can directly affect ATPase (see Fig. 4). The data with E. hirae mutant MS116 confirmed this suggestion, as the results were similar to the effects with wild-type strain but were expressed in much less content. Such differences might be connected with the FOF1-ATPase which is defective in this strain. There are a lot of studies confirming the fact that ATPase can be a target for several external factors, such as antibiotics and heavy metals [5, 6, 37]. Similar effects were observed by Chichova et al. with mammalian cells either [38], showing that Ag nanoparticles inhibited mitochondrial ATPase activity of rat liver cells. As the FOF1-ATPase has a crucial role in cell metabolism, such effects can be defining for bacterial growth and survival.

Fig. 4
figure 4

Proposed scheme for Ag nanoparticles effects on bacteria. Ag nanoparticles are suggested to affect H+-coupled membrane transport of bacteria. E. coli and E. hirae possessed H+–K+ exchange through FOF1 and K+-transport system (left side). In the case of E. hirae Ag nanoparticles changed the stoichiometry of H+–K+ exchange through membrane. The effect on FOF1 and disturbance of the interaction between FOF1 and K+-transport system (right side) might be responsible for stronger antibacterial effects with E. hirae

Full size image

Conclusions and significance

The results pointing out the role of the FOF1-ATPase in bacterial response to Ag nanoparticles are absolutely novel and important especially for E. hirae. These findings can be decisive in understanding the mechanisms of the effects of metal nanoparticles on different bacteria. This information might be helpful while using nanoparticles as antibacterial agents in biotechnology and other applications.

Methods

Bacterial strains and growth, Eh

This study was performed with E. hirae ATCC9790 wild type strain and the atpD mutant strain MS116 (lacked β subunit in F1) and E. coli K-12 wild-type strains. E. hirae was supplied by Prof. H. Kobayashi (Graduate School of Pharmaceutical Sciences, Chiba University, Chiba 263, Japan) and Prof. M. Solioz (Department of Clinical Pharmacology, University of Bern, Bern 3010, Switzerland) [22]. E. coli was laboratory stock strain.

E. hirae was grown under anaerobic conditions 37 °C in the medium that contains 1 % tryptone, 0.5 % yeast extract, 1 % K2HPO4 with addition of 0.2 % glucose at pH 8.0 [22, 23]. E. coli was grown in peptone (2 % peptone, 0.5 % NaCl) medium buffered with 0.1 M K2HPO4 (pH 7.5), 0.2 % glucose was added [39]. The pH of the medium was measured with pH-selective electrode (HJ1131B, Hanna Instruments, Portugal) and adjusted by 0.1 M NaOH or HCl. The bacterial growth rate was determined by measuring the changes in optical density (OD) of bacterial suspension using a spectrophotometer (Spectro UV–vis Auto, Labomed, USA) at a wave length of 600 nm. Bacterial growth was monitored every hour till 8 h and at 24 h. The bacterial suspension was washed and concentrated by centrifugation at 3600g for 15 min and transferred into appropriate medium.

The latent (lag) phase duration was determined as described previously [5]. The specific growth rate was calculated by dividing 0.693 (lg2 = 0.693) by the doubling time of OD in the ranges where the changes in the logarithm of OD depended on time in a linear manner.

Nanoparticles susceptibility

TiO2 and ZnO thin films with nanostructured surface deposited on sapphire substrate, microporous Cu2O tablet with nano-scale roughness of surface and concentrated Ag nanoparticles colloid solution were used. As a colloid solution of Ag nanoparticles we used “Biocidal Additive” produced by Concern “Nano-industry” (Moscow, Russia). Ag nanoparticles had sizes in the range from 3 to 15 nm; optimal sizes were of 10–12 nm (Fig. 5).

Fig. 5
figure 5

Ag nanoparticles distribution in the colloid solution depending on their size. For source of Ag nanoparticles, see “Methods”

Full size image

This water solution consists of 0.21 mg/cm3 Ag nanoparticles and 18.75 mg/cm3 DSS.The latter is an anionic surfactant, a substance that lowers the surface tension of water and it is found that good water solubilizing capacity is depended on its structure [40].

The microporous Cu2O tablets were prepared by pressing of CuO micro-scale (1–10 μm) powder and posterior annealing during 3 h at 800 °C in the ambient of oxygen at 1 mbar pressure. In accordance with Cu–O phase diagram [41] at these annealing conditions due to the chemical reaction 4CuO → 2Cu2O + O2 the molecules of CuO loses oxygen and transforms into Cu2O. This phenomenon results in formation of nanoscale roughness on the surface of Cu2O film in the range ±500 nm [42]. Susceptibility of microorganisms to nanoparticles was studied by determining bacterial growth in the presence of the nanoparticles. Sapphire base plates with deposited nanoparticles and concentrated Ag nanoparticles colloid solution were added both in bacterial growth medium where lag phase duration and specific growth rate were determined [37] and on agar plates [43]. As in the case of antibiotics, susceptibility of bacteria to nanoparticles was observed by determination of standardized agar diffusion zones (halos) indicating about bacterial growth inhibition. Bacterial suspension of 100 µl was disseminated on plates; disks with deposited nanoparticles were placed on agar and incubated in 37 °C for 24 h. After the incubation agar halos were observed and diameters were measured.

ATPase assay

ATPase activity of membrane vesicles was measured by amount of liberated inorganic phosphate (Pi) after adding 5 mM ATP by a spectrophotometric method [44, 45]. The assay mixture was 50 mM Tris–HCl (pH 8.0), containing 0.4 mM MgSO4 and 100 mM KCl. When it was necessary, membrane vesicles were pre-incubated with nanoparticles or DCCD for 10 min. The corrections were made for blanks without ATP or membrane vesicles. Relative ATPase activity was expressed in nmol Pi per mg protein in 1 min. Membrane vesicles were isolated as described earlier [46] except that the buffers lacked K+.

Proton-potassium exchange assays

Transport of H+ and K+ through the membrane in the whole cells was assayed by monitoring changes in their activity in the medium using appropriate selective electrodes (HJ1131B, Hanna Instruments, Portugal, and PVC membrane type, Cole Parmer Instruments Co., USA) as described elsewhere [22, 36]. Ions fluxes are expressed as the change in external activity of the ion in mM/min/1010 cells in a unit of medium volume (ml). Electrode readings data were outputted automatically by LabView computer program (National Instruments Co., USA). Using this program, electrode readings were calibrated by titration the assay medium (200 mM Tris–phosphate buffer (pH 8.0) containing 0.4 mM MgSO4, 1 mM NaCl and 1 mM KCl) with 0.01 N HCl and 0.02 mM KCl. When mentioned, cells were treated with metal nanoparticles and/or DCCD (0.1 mM) for 10 min prior assays. Preparation of whole cells for determination of ion fluxes was described before [22].

Data processing and reagents

The average data are presented from 3 independent measurements. The standard errors calculated using Microsoft Excel 2013 do not exceed 3 % (if not mentioned). The validity of the differences between the changes obtained and the controls are estimated by Student P value: if there is no other value, then p < 0.01.

Glucose (Borisov Plant of Medicinal Preparations, Belarus), agar, DCCD (“Sigma”, USA), tryptone, yeast extract, Tris (amino-methane) (“Carl Roth GmbH & Co”, Germany) as well as the other reagents of analytical grade were used in the study.

Abbreviations

DCCD:

N,N′-dicyclohexylcarbodiimide

DSS:

dioctyl sodium sulfosuccinate

FOF1-ATPase:

proton translocating ATPase

References

  1. Ansari MA, Khan HM, Khan AA, Malik A, Sultan A, Shahid M, et al. Evaluation of antibacterial activity of silver nanoparticles against MSSA and MRSA on isolates from skin infections. Biol Med. 2011;3:141–6.

    CAS  Google Scholar 

  2. Hajipour M, Fromm K, Ashkarran A, Jimenez de Aberasturi D, deLarramendi IR, Rojo T, et al. Antibacterial properties of nanoparticles. Trends Biotechnol. 2012;30:499–511.

    Article  CAS  Google Scholar 

  3. Baker-Austin C, Wright M, Stepanauskas R, McArthur JV. Co-selection of antibiotic and metal resistance. Trends Microbiol. 2006;14:176–82.

    Article  CAS  Google Scholar 

  4. Bhati-Kushwaha H, Malik CP. Assessment of antibacterial and antifungal activities of silver nanoparticles obtained from the Callus (stem and leaf) of Tridax procumbens L. Ind J Biotechnol. 2014;13:114–20.

    CAS  Google Scholar 

  5. Vardanyan Z, Trchounian A. The effects of copper (II) ions on Enterococcus hirae cell growth and the proton-translocating FoF1 ATPase activity. Cell Biochem Biophys. 2010;57:19–26.

    Article  CAS  Google Scholar 

  6. Vardanyan Z, Trchounian A. Fe(III) and Fe(II) ions different effects on Enterococcus hirae cell growth and membrane-associated ATPase activity. Biochem Biophys Res Commun. 2012;417:541–5.

    Article  CAS  Google Scholar 

  7. Mijnendonckx K, Leys N, Mahillon J, Silver S, Van Houdt R. Antimicrobial silver: uses, toxicity and potential for resistance. Biometals. 2013;26:609–21.

    Article  CAS  Google Scholar 

  8. Manivasagan P, Venkatesan J, Senthilkumar K, Sivakumar K, Kim SK. Biosynthesis, antimicrobial and cytotoxic effect of silver nanoparticles using a novel Nocardiopsis sp. MBRC-1. Biomed Res Int. 2013;2013:287638.

    Google Scholar 

  9. Lu C, Brauer MJ, Botstein D. Slow growth induces heat-shock resistance in normal and respiratory-deficient yeast. Mol Biol Cell. 2009;20:891–903.

    Article  CAS  Google Scholar 

  10. Shahverdi AR, Fakhimi A, Shahverdi HR, Minaian S. Synthesis and effect of silver nanoparticles on the antibacterial activity of different antibiotics against Staphylococcus aureus and Escherichia coli. Nanomedicine. 2007;3:68–171.

    Google Scholar 

  11. Fabrega J, Fawcett SR, Renshaw JC, Lead JR. Silver nanoparticle impact on bacterial growth: effect of pH, concentration and organic matter. Environ Sci Technol. 2009;43:7285–90.

    Article  CAS  Google Scholar 

  12. Morones JR, Elechiguerra JL, Camachoet A, Holt K, Kouri JB, Ramírez JT, et al. The bactericidal effect of silver nanoparticles. Nanotechnology. 2005;16:2346–53.

    Article  CAS  Google Scholar 

  13. Pal S, Tak YK, Song JM. Does the antibacterial activity of silver nanoparticles depend on the shape of the nanoparticle? A study of the gram-negative bacterium Escherichia coli. Appl Environ Microbiol. 2007;73:1712–20.

    Article  CAS  Google Scholar 

  14. Nadtochenko VA, Radzig MA, Khmel IA. Antibacterial action of metal and semiconductor nanoparticles. Russ Nanotechnol. 2010;5:277–89 (in Russian).

    Article  Google Scholar 

  15. Zhao GJ, Stevens SE. Multiple parameters for the comprehensive evaluation of the susceptibility of Escherichia coli to the silver ion. Biometals. 1998;11:27–32.

    Article  CAS  Google Scholar 

  16. Arokiyaraj S, Islam VIH, Bharanidraran R, Raveendar S, Lee J, Kim DH, et al. Antibacterial, anti-inflammatory and probiotic potential of Enterococcus hirae isolated from the rumen of Bos primigenius. World J Microbiol Biotechnol. 2014;30:2111–8.

    Article  CAS  Google Scholar 

  17. Foulquié Moreno M, Sarantinopoulos P, Tsakalidou E, De Vuyst L. The role and application of enterococci in food and health. Int J Food Microbiol. 2006;106:1–24.

    Article  Google Scholar 

  18. Iseppi R, Pilati F, Marini M, Toselli M, de Niederhhausern S, Guerrieri E, et al. Anti-listerial activity of a polymeric film coated with hybrid coatings doped with Enterocin 416K1 for use as bioactive food packaging. Int J Food Microbiol. 2008;123:281–7.

    Article  CAS  Google Scholar 

  19. Lee S-M, Choi M-H, Hong W-K, Park JM, Yu A, Lee J-S, et al. Production of mixed cids from non-pretreated red algae Gelidium amansii. Renew Energy. 2014;63:366–9.

    Article  CAS  Google Scholar 

  20. Subramanian MR, Tallun S, Christopher LP. Production of lactic acid using a new homofermentative Enterococcus faecalis isolate. Microb Biotechnol. 2015;8:221–9.

    Article  CAS  Google Scholar 

  21. Azócar I, Vargas E, Duran N, Arrieta A, González E, Pavez J, et al. Preparation and antibacterial properties of hybrid-zirconia films with silver nanoparticles. Mat Chem Phys. 2012;137:396–403.

    Article  Google Scholar 

  22. Trchounian A, Kobayashi H. Relationship of K+-uptaking system with H+-translocating ATPase in Enterococcus hirae, growth at a high or low alkaline pH. Curr Microbiol. 1998;36:114–8.

    Article  CAS  Google Scholar 

  23. Poladyan A, Kirakosyan G, Trchounian A. Growth and proton-potassium exchange in the bacterium Enterococcus hirae: the effect of protonofore and the role of redox potential. Biophys. 2006;51:447–51.

    Article  Google Scholar 

  24. Hawkins M, Soon-Shiong P, Desai N. Protein nanoparticles as drug carriers in clinical medicine. Adv Drug Deliv Rev. 2008;60:876–85.

    Article  CAS  Google Scholar 

  25. Pantic I. Application of silver nanoparticles in experimental physiology and clinical medicine: current status and future prospects. Rev Adv Mater Sci. 2014;37:15–9.

    Google Scholar 

  26. Kakinuma Y. Inorganic cation transport and energy transduction in Enterococcus hirae and other streptococci. Microbiol Mol Biol Rev. 1998;62:1021–45.

    CAS  Google Scholar 

  27. Yoon K, Byeon J, Park J, Hwang J. Susceptibility constants of Escherichia coli and Bacillus subtilis to silver and copper nanoparticles. Sci Total Environ. 2007;373:572–5.

    Article  CAS  Google Scholar 

  28. Premanathan M, Karthikeyan K, Jeyasubramanian K, Manivannan G. Selective toxicity of ZnO nanoparticles toward Gram-positive bacteria and cancer cells by apoptosis through lipid peroxidation. Nanomedicine. 2011;7:184–92.

    Article  CAS  Google Scholar 

  29. Azam A, Ahmed A, Oves M, Khan MS, Habib SS, Memic A, et al. Antimicrobial activity of metal oxide nanoparticles against Gram-positive and Gram-negative bacteria: a comparative study. Int J Nanomedicine. 2012;7:6003–9.

    Article  CAS  Google Scholar 

  30. Lara HH, Garza-Treviño EN, Ixtepan-Turrent L, Singh DK. Silver nanoparticles are broad-spectrum bactericidal and virucidal compounds. J Nanobiotechnol. 2011;9:30–8.

    Article  CAS  Google Scholar 

  31. Lok CN, Ho CM, Chen R, He QY, Yu WY, Sun H, et al. Proteomic analysis of the mode of antibacterial action of silver nanoparticles. J Proteome Res. 2006;5:916–24.

    Article  CAS  Google Scholar 

  32. Gibbins B, Warner L. The role of antimicrobial silver nanotechnology. Med Device Diagnostic Indust Mag. 2005;1:1–2.

    Google Scholar 

  33. Raffi M, Hussain F, Bhatti TM, Akhter JI, Hameed A, Hasanet MM. Antibacterial characterization of silver nanoparticles against E. coli ATCC-15224. J Mater Sci Technol. 2008;24:192–6.

    CAS  Google Scholar 

  34. Rai M, Yadav A, Gade A. Silver nanoparticles as a new generation of antimicrobials. Biotechnol Adv. 2009;27:76–83.

    Article  CAS  Google Scholar 

  35. Kawano M, Igarashi K, Kakinuma Y. Isolation of Enterococcus hirae mutant deficient in low-affinity potassium uptake at alkaline pH. Biosci Biotech Biochem. 2002;66:1597–600.

    Article  CAS  Google Scholar 

  36. Trchounian A. Escherichia coli proton-translocating FOF1 ATP synthase and its association with solute secondary transporters and/or enzymes of anaerobic oxidation-reduction under fermentation. Biochem Biophys Res Commun. 2004;315:1051–7.

    Article  CAS  Google Scholar 

  37. Torgomyan H, Trchounian A. Bactericidal effects of low-intensity extremely high frequency electromagnetic field: an overview with phenomenon, mechanisms, targets and consequences. Crit Rev Microbiol. 2013;39:102–11.

    Article  CAS  Google Scholar 

  38. Chichova M, Shkodrova M, Vasileva P, Kirilova K, Doncheva-Stoimenova D. Influence of silver nanoparticles on the activity of rat liver mitochondrial ATPase. J Nanoparticle Res. 2014;16:2243.

    Article  Google Scholar 

  39. Mnatsakanyan N, Bagramyan K, Vassilian A, Vardanian V, Zakharyan E, Vassilian A, et al. Relationship of the Escherichia coli TrkA system of potassium ion uptake with the FOF1-ATPase under growth conditions without anaerobic or aerobic respiration. Biosci Rep. 2002;22:421–30.

    Article  CAS  Google Scholar 

  40. Palanisamy P, Raichur AM. Synthesis of NiO nanoparticles by water-in-oil microemulsion technique. Int Res J Pure Appl Chem. 2014;4:494–506.

    Article  Google Scholar 

  41. Klug HP, Alexander LE. X-Ray Diffraction Procedure for Polycrystalline and Amorphous Materials. New York: Wiley; 1974.

    Google Scholar 

  42. Gevorgyan V, Reymer A, Nersesyan M, Nitsche S, Giorgio S, Karapetyan A, et al. Properties of nano-structured cuprous oxide thin films fabricated by thermal oxidation of copper layer. Proc SPIE. 2011;8414:841406.

    Article  Google Scholar 

  43. Bauer AW, Kirby WM, Sherris JC, Turck M. Antibiotic susceptibility testing by a standardized single disk method. Am J Clin Pathol. 1966;45:493–6.

    CAS  Google Scholar 

  44. Blbulyan S, Avagyan A, Poladyan A, Trchounian A. Role of different Escherichia coli hydrogenases in H+ efflux and F1FO-ATPase activity during glycerol fermentation at different pH values. Biosci Rep. 2011;31:179–84.

    Article  CAS  Google Scholar 

  45. Blbulyan S, Trchounian A. Impact of membrane-associated hydrogenases on the FOF1-ATPase in Escherichia coli during glycerol and mixed carbon fermentation: ATPase activity and its inhibition by N, N′-dicyclohexylcarbodiimide in the mutants lacking hydrogenases. Arch Biochem Biophys. 2015;579:67–72.

    Article  CAS  Google Scholar 

  46. Kirakosyan G, Trchounian K, Vardanyan Z, Trchounian A. Copper (II) ions affect Escherichia coli membrane vesicles’ SH-groups and a disulfide-dithiol interchange between membrane proteins. Cell Biochem Biophys. 2008;51:45–50.

    Article  CAS  Google Scholar 

Download references

Authors’ contributions

ZV performed the cultivation and heavy metal nanoparticles effectsstudy on bacteria; VG obtained heavy metal oxides thin films with nanostructured surfaces and prepared nanoparticles; ZV, VG wrote the manuscript; MA obtained nanoparticles and supplied some reagents, HV discussed and revised the manuscript; AT supervised and coordinated the research, edited the manuscript. All authors have read and approved the manuscript.

Acknowledgements

We express our gratitude to Prof. H. Kobayashi and Prof. M. Solioz for supplying E. hirae strains. This study was financed by Basic support from the State Committee of Science, Ministry of Education and Science of Armenia (#10-3/9).

Competing interests

The authors declare that they have no competing interests.

Author information

Authors and Affiliations

  1. Research Institute of Biology, Faculty of Biology, Yerevan State University, 1 A. Manoukian Str., 0025, Yerevan, Armenia

    Zaruhi Vardanyan & Armen Trchounian

  2. Department of Materials Technology and Structures of Electronic Technique, Institute of Mathematics and High Technologies, Russian-Armenian (Slavonic) University, 123 H. Emin Str., 0051, Yerevan, Armenia

    Vladimir Gevorkyan

  3. “Nano-industry” Concern, 4 Bardin Str., 1 bulk, 119334, Moscow, Russia

    Michail Ananyan

  4. Department of Medicinal Biochemistry and Biotechnology, Institute of Mathematics and High Technologies, Russian-Armenian (Slavonic) University, 123 H. Emin Str., 0051, Yerevan, Armenia

    Hrachik Vardapetyan & Armen Trchounian

  5. Department of Microbiology, Microbes and Plants Biotechnology, Faculty of Biology, Yerevan State University, 1 A. Manoukian Str., 0025, Yerevan, Armenia

    Armen Trchounian

Authors
  1. Zaruhi Vardanyan
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Vladimir Gevorkyan
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Michail Ananyan
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Hrachik Vardapetyan
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Armen Trchounian
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Armen Trchounian.

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Vardanyan, Z., Gevorkyan, V., Ananyan, M. et al. Effects of various heavy metal nanoparticles on Enterococcus hirae and Escherichia coli growth and proton-coupled membrane transport. J Nanobiotechnol 13, 69 (2015). https://doi.org/10.1186/s12951-015-0131-3

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s12951-015-0131-3

Keywords

Journal of Nanobiotechnology

ISSN: 1477-3155

Contact us