Rough surface Au@Ag core–shell nanoparticles to fabricating high sensitivity SERS immunochromatographic sensors

Abstract

Immunochromatographic sensors (ICSs) are inexpensive, simple, portable, and robust, thus making ICSs commonplace in clinical diagnoses, food testing, and environmental monitoring. However, commonly used gold nanoparticles (AuNPs) ICSs have low sensitivity. Therefore, we developed highly sensitive surface enhanced Raman scattering (SERS) ICSs. To enhance the sensitivity of SERS ICSs, rough surface core–shell Au@Ag nanoparticles (RSAu@AgNPs) were prepared by coating silver on the surface of gold nanoflowers (AuNFs). Then these nanoparticles were used as SERS substrate in the SERS ICSs, after which the SERS ICSs were implemented to detect haemoglobin and heavy metal cadmium ion (Cd2+). The limit of detection (LOD) of the SERS ICSs for detecting haemoglobin was 8 ng/mL, and the linear range of the SERS ICSs was from 31.3 to 2000 ng/mL. The LOD of the SERS ICSs for detecting Cd2+ was 0.05 ng/mL and the linear analysis range was from 0.05 to 25 ng/mL. The cross reactivity of the SERS ICSs was studied and results showed that the SERS ICSs exhibited highly specific for detection of haemoglobin and Cd2+, respectively. The SERS ICSs were then used to detect haemoglobin (spiked in serum and in stool) and Cd2+ (spiked in tap water, river water, and soil leaching water), and the results showed high recovery. These characteristics indicated that SERS ICSs were ideal tools for clinical diagnosis and environmental pollution monitoring.

Background

Due to their low cost, robustness, convenience and rapidity, immunochromatographic sensors (ICSs) have been extensively used in medicine, agriculture, and over-the-counter personal use, such as pregnancy tests [15]. Many kinds of materials, such as colloidal gold [6], colloidal carbon [7], liposome [8, 9], quantum dots [10, 11], fluorescent nanoparticles [12], and organic fluorescent dyes [13] were used as racers in ICSs. Among the aforementioned materials, AuNPs were widely adopted, due to their vivid color, ease of synthesis, low cost, and excellent chemical stability. However, when compared with laboratory based methods, the sensitivity of most AuNPs ICSs to detect biomarkers was significantly less than other methods, such as enzyme-linked immunoassay (ELISA). Consequently, AuNPs ICSs are not particularly useful for detecting lower concentration biomarkers. Compared with AuNPs ICSs, fluorescent ICSs exhibit higher sensitivity (10-30 times higher than AuNPs ICSs). Currently used fluorescent tracers in ICSs are organic fluorescent dyes, fluorescent nanoparticles, and quantum dots. However, organic fluorescent dyes such as FITC are known to be photo-unstable and have relatively low fluorescence intensities. Even though fluorescent nanoparticles have high fluorescence intensity, excellent photo-stability, and high conjugation efficiency, both organic fluorescent dyes and fluorescent nanoparticles have a relatively small Stokes shift that often leads to fluorescent ICSs suffering from background interference. Another fluorescent tracer currently used in ICSs is quantum dots. This is because of the excellent features of quantum dots: they have very high levels of brightness, size-tunable fluorescence emission, narrow spectral line widths, large absorption coefficients, and excellent stability against photo-bleaching. However, the price of quantum dots is currently relatively high.

Surface-enhanced Raman scattering (SERS) based sensors provide the potential for rapid, high-throughput, sensitive detection. SERS have been used for cell imaging [1416], tumor diagnosis [1719], enzyme activity analysis [20, 21], nucleic acids analysis [2224], gene mutations analysis [25], immune sensors [26, 27], and aptamer sensors [28, 29]. Over the past decade, the SERS field has witnessed many achievements, including a theoretical study of SERS [30, 31], the development of portable and high-performance Raman spectrometers [3235], and the fabrication of highly sensitive, uniform, and reproducible SERS substrates [36, 37]. These important studies provide the basis for many SERS applications. AuNPs and silver nanoparticles (AgNPs) are the most widely used substrates for SERS. The SERS enhancement factor of AgNPs was demonstrated to be higher than that of AuNPs. It has been theoretically predicted and experimentally confirmed that sharp metallic protrusions and nano-gaps, called ‘hot spots’, are essential for a stronger SERS response [3840]; these include: nanoflowers, nanosatellites, nanourchins, nanostars, etc. In addition, Au@Ag core–shell nanoparticles exhibit a higher SERS efficiency than AuNPS or AgNPs under near-infrared excitation [41]. Xie reported flower-like AuNPs (three-dimensional branched nanoparticles with more than 10 tips) that exhibited strong Raman enhancement factors [42]. During our research, to obtain higher enhanced efficient SERS substrate, we coated silver on AuNFs to prepare higher SERS efficiency rough surface Au@Ag core–shell nanoparticles (RSAu@AgNPs). These nanoparticles were used to fabricate the highly sensitive SERS ICSs. We used the developed SERS ICSs to detect haemoglobin and Cd2+. The results showed that SERS ICSs have a high sensitivity and high recovery. These characteristics indicated that SERS ICSs were ideal tools for clinical diagnosis and environmental pollution monitoring.

Experimental

Reagents and materials

Chloroauric acid (HAuCl4, 99.99 %), silver nitrate (99.80 %), HEPES, 4-mercapto-benzoic acid (4-MBA), and ascorbic acid were obtained from Sigma-Aldrich (Shanghai, China). Other metal powders were purchased from Merck Chemical (Darmstadt, Germany). Nitrocellulose (NC) membranes were purchased from Millipore (Shanghai, China). Plastic backing, conjugation pads, sample pads and absorbent pads were purchased from Shanghai JieNing Bio-tech (Shanghai, China). Anti-Cd2+-EDTA monoclonal antibodies (mAb) and BSA-Cd2+-EDTA were prepared in our laboratory (Additional file 1). A couple of Anti-haemoglobin monoclonal antibodies and haemoglobin were gifted from Guangzhou Weimi Bio-Tech CO., LTD.

Equipment

A field-emission transmission electron microscope (TEM, Philips, Holland), centrifuge (Beckman, Germany), and ICP-MASS (Thermo-Fisher, USA) were used. An XYZ 3200 series dispense system (Bio-Dot Scientific Equipment, Pvt. Ltd.), a programmable HGS201 strip cutter (purchased locally in Shanghai, China), and an Advantage 785 Near Infrared (NIR) Raman Spectrometer (SciAps, Inc.) were also used in this study (laser power60 mW).

Preparation of RSAu@AgNPs

AuNFs were synthesized following a previous research paper [42]. In a typical experiment, 0.2 mL of 25 mM HAuCl4 was added to 10 mL of a 20 mM HEPES solution (pH 7.4). The formation of AuNFs was indicated when the initially light-yellow mixture changed to purple within approximately 30 min. The AuNFs were then stored at 4 °C until further use. RSAu@AgNPs were synthesized as follows: 40 µL of 0.1 M NaOH and 30 µL of 0.1 M ascorbic acid were added to 1 mL of the AuNFs. After shaking vigorously, 400 μL of 10 mM AgNO3 was added to the above solution. Following this addition, the mixture was again shaken vigorously and the color of the solution changed rapidly from purple to yellow, indicating the formation of RSAu@AgNPs. Preparations of AuNPS, AgNPs, and Au@AgNPs are displayed in Additional file 1.

Preparation of mAb-RSAu@AgNPs-4MBA

A total of 0.2 μL of 10 mM 4-MBA contained in ethanol was added to 1 mL of the prepared RSAu@AgNPs, which was then shaken vigorously for 1 h. Then, 3 μL of 1 mg/mL monoclonal antibody (mAb) and 15 μL of 1 mg/mL PVP were added simultaneously to the above-mentioned solution and were shaken vigorously. After incubating at room temperature for 30 min, 100 μL of 10 mg/mL PVP was used to cover the surface of the RSAu@AgNPs for 1 h. The resulting colloid was centrifuged at 7000 rpm for 10 min. Then, this supernatant was discarded and the remaining pellet was suspended in 200 μL of dilution buffer [15 mM PB buffer (pH 8.0) containing 1 % (w/v) BSA, 20 % (w/v) sucrose, 20 % (w/v) trehalose, 1 % (w/v) Tween-20, and 0.02 % sodium azide]; it was then stored at 4 °C for further use.

Fabrication of SERS ICSs

Prepared SERS ICSs for detecting Cd2+: coating antigen Cd2+-EDTA-BSA (0.1 mg/mL) was dispensed on the specified area of an NC membrane that was designated as the test line (T-line) by using an automatic dispenser with a volume of 1 μL/cm. The NC membrane was dried at 37 °C for 24 h. Sample pad was pre-treated with 0.01 M PBS buffer (pH 7.2), containing 0.5 % (w/v) BSA and 2 % Triton X-100. Using a dilution buffer, the mAb-RSAu@AgNPs-4MBA was diluted 64 times and then dispensed on the conjugate pad using the automatic dispenser with a volume of 2 μL/cm. After the pads were dried at 37 °C for 2 h, all components of the SERS ICSs were assembled with 2 mm overlaps. These stacks were then cut into ICSs strips and placed into plastic housings. Prepared SERS ICSs for detecting haemoglobin: mAb-RSAu@AgNPs-4MBA was diluted 32 times and then dispensed on NC membrane at T-line. Other similar processes to SERS ICSs for detecting Cd2+ were applied.

Performance of the SERS ICSs

For detecting haemoglobin: A series of concentrations of a haemoglobin solution (60 μL) in PBS was detected using the SERS ICSs. After 15 min, Raman signals of these ICSs were recorded using a portable Raman spectrometer with an integration time of 20 s. For detecting Cd2+: Cd2+ solution was diluted to a series of concentrations by 50 nM EDTA-Na2 and detected by using SERS ICSs. After 15 min, the Raman signals of these ICSs were recorded as mentioned above. SERS ICSs detection of haemoglobin or Cd2+ in spiked samples is displayed in Additional file 1. Additionally, experimental procedures that study the specificity and recovery of SERS ICSs are displayed in Additional file 1.

Results and discussion

Synthesis and characterization of nanoparticles

AuNFs were synthesized using HEPES to reduce the chloroauric acid and were coated with a silver shell by reducing AgNO3 to elemental silver. We optimized the SERS efficiency of RSAu@AgNPs and showed that RSAu@AgNPs exhibited higher SERS efficiency by adding 400 μL 10 mM AgNO3 in 1 mL AuNFs (Additional file 1: Figure S4). Figure 1b–c show typical TEM images of the AuNFs, RSAu@AgNPs. Compared with AuNPs (Additional file 1: Figure S1), AgNPs (Additional file 1: Figure S2) and Au@AgNPs (Additional file 1: Figure S3), the RSAu@AgNPs surfaces are much rougher (Fig. 1b). AuNFs exhibited an SPR peak at 560 nm; whereas, the RSAu@AgNPs and mAb-RSAu@AgNPs-4MBA presented an SPR peak at 420 nm, indicating that the silver had successfully coated the surfaces of AuNFs (Additional file 1: Figure S6). Figure 1d shows the Raman signal intensity of the reporter molecule 4-MBA enhanced by the AuNFs, AuNPs, Au@AgNPs, RSAu@AgNPs and mAb-RSAu@AgNPs-4MBA. To accurately assess the SERS activity of these nanomaterials, the same amount of 4-MBA was added to an equal volume of each of the nano-materials with the same concentration. After optimization of 4-MBA concentration conjugate with RSAu@AgNPs-4MBA (Additional file 1: Figure S5), 0.2 μL of 10 mM 4-MBA was mixed with 1 mL of nanomaterials at room temperature. After 1 h, the SERS spectra were detected with exposure times of 20 s. The SERS spectrum of 4-MBA was characterized by peaks at 1077 cm−1. The SERS intensities of the RSAu@AgNPs-4MBA and mAb-RSAu@AgNPs-4MBA were considerably higher than those of the AuNPs-4MBA, AuNFs-4MBA, AgNPS-4MBA, and Au@AgNPs-4MBA. These results indicated that core–shell structures and rough surfaces give higher SERS efficiency to RSAu@AgNPs. These results are consistent with previous reports [41, 43].

Fig. 1
figure 1

Synthesis and characterization of mAb-RSAu@AgNPs-4MBA. a Schematic diagram of synthesized mAb-RSAu@AgNPs-4MBA. bc TEM images of AuNFs and RSAu@AgNPs, scale bars were 50 nm. d Comparisons: SERS efficiency of AuNFs-4MBA, RSAu@AgNPs-4MBA and mAb-RSAu@AgNPs-4MBA, AuNPs-4MBA, AgNPs-4MBA and Au@AgNPs-4MBA. The Raman signal was detected in 96-well micro-plates, and the exposure time was 20 s

The SERS ICSs to detect haemoglobin

In clinical studies, hemoglobin is an important biomarker for diagnosing intestinal bleeding. In this study, we prepared SERS ICSs and used them to detect haemoglobin. The SERS ICSs for detecting haemoglobin consisted of five components (from top to bottom): (a) a sample pad for applying samples, (b) a conjugate pad for loading mAb-RSAu@AgNPs-4MBA, (c) a 25 mm NC membrane acting as the chromatography matrix, (d) an absorbent pad serving as the liquid sink, and (e) a plastic backing for supporting all the components (Fig. 2a). The capture mAb was dispensed on the NC membrane at T-line. The principle of the SERS ICSs is shown in Fig. 2b–c. When negative samples (not containing analytes) were applied, the liquid samples dispersed mAb-RSAu@AgNPs-4MBA that were preloaded on the conjugation pad and made the mAb-RSAu@AgNPs-4MBA migrate toward the absorbent pad. Hemoglobin did not bind with mAb-RSAu@AgNPs-4MBA; therefore, when samples reached T-line zone, mAb-Au@AgNPs-4MBA could not bind to the coating mAb at T-line. Subsequently, a weak SERS signal at T-line was detected. In contrast, when a certain amount of haemoglobin solution was applied to the sample pad, haemoglobin would first bind to the mAb-RSAu@AgNPs-4MBA; these nanoparticles were then captured by mAb at T-line and a strong Raman signal was detected. Raman signal intensity of the ICSs at T-line increased, as concentrations of haemoglobin elevated. To facilitate the analysis of the detection results, we chose Raman intensity at the peak of 1077 cm−1 as the test signal and the integration times of the ICSs test were maintained at 20 s.

Fig. 2
figure 2

a Schematic diagram of the SERS ICSs for detecting haemoglobin. The SERS ICSs consists of five overlapping layers: absorption pad, NC membrane, conjugation pad and sample pad, which were placed on a plastic backing. Capture mAb was dispensed at T-line. When the SERS ICSs detected negative samples, Raman signal at T-line was weak; whereas, when the SERS ICSs detected positive samples, Raman signal at T-line was strong. b Concentration dependent SERS spectra of SERS ICSs obtained from detecting different concentrations of haemoglobin: The entire SERS spectra are shown in Additional file 1: Figure S10–21. Detailed vibrational assignments of Raman peaks are presented in Additional file 1: Table S1. c Calibration curve of SERS ICSs for the detection of haemoglobin

The surfactant triton X-100 accelerated the diffusion speed of mAb-RSAu@AgNPs-4MBA at NC membrane, thereby, reducing the time taken for SERS to detect haemoglobin. However, a high concentration of surfactant triton X-100 reduced the amount of time that mAb-RSAu@AgNPs-4MBA stayed at T-line and decreased the sensitivity of SERS ICSs. Considering the detection time and sensitivity of the SERS ICSs, 2 % triton X-100 was contained in sample pad treatment agent (Additional file 1: Figure S7). Following these procedures, concentrations of mAb-RSAu@AgNPs-4MBA that dispersed on conjugation pad, which impacted the performance of ICSs, were optimized. A high concentration of mAb-RSAu@AgNPs-4MBA dispersed on conjugation pad enhanced the sensitivity of SERS ICS; however, this also may have increased the background SERS signal on nitrocellulose membrane. Considering the background SERS signal and sensitivity of the SERS ICSs, mAb-RSAu@AgNPs-4MBA was diluted 32 times and then dispersed on conjugation pad (Additional file 1: Figure S8).

The results for detecting a series of concentrations of haemoglobin are shown in Fig. 2b–c. The detection time was chosen as 15 min (Additional file 1: Figure S9). When negative samples were applied to the SERS ICSs, the Raman signal intensity at T-line was 492 a.u. When haemoglobin concentrations were higher than 15.6 ng/mL, SERS signal at T-line showed a gradual increase. When haemoglobin concentrations were higher than 16,000 ng/mL, SERS signal at T-line remained at approximately 24,500 a.u. The calibration curve of SERS ICSs for detecting haemoglobin had a positive slope, with a linear detection range from 32.3 to 2000 ng/mL. The LOD of SERS ICSs was 8 ng/mL, calculated by a concentration response to the SERS intensity (SRES intensity of negative sample + 3 × SD).

The SERS ICSs for detecting Cd2+

To demonstrate that SERS ICSs were appropriate for detecting small molecules, we further used them to detect heavy metal cadmium (Cd2+). Cd2+ is believed to have a biological half-life of greater than 10 years in the human body. Humans are exposed to cadmium predominantly through the ingestion of cadmium contaminated food, water, and soil, or through the inhalation of cadmium-containing dusts. After ingestion, cadmium accumulates in the kidneys, liver, lungs, and gastrointestinal tract, where it can then cause progressively toxic effects, including cancer and renal damage [44, 45]. Because Cd2+ is too small to be recognized by antibodies, EDTA-2Na was selected to chelate Cd2+ to form a specific hapten. To prepare the complete antigen, iEDTA was used to conjugate Cd2+ and link the carrier proteins. To prepare SERS ICSs for detecting Cd2+: Cd2+-EDTA-BSA was dispersed at T-line and anti-Cd2+-EDTA mAb labeled RSAu@AgNPs-4MBA were dispersed on conjunction pad. The principle of the SERS ICSs that detected Cd2+ is shown in Fig. 3. When negative samples (containing no analytes) were applied, mAb-RSAu@AgNPs-4MBA were dispersed in samples and migrated toward the absorbent pad. When samples reached T-line zone, mAb-RSAu@AgNPs-4MBA bound to Cd2+-EDTA-BSA at T-line and the SERS signal was detected. In contrast, when a certain amount of positive sample solution was applied, Cd2+-EDTA would first bind to the mAb-RSAu@AgNPs-4MBA. Then, the amount of mAb-RSAu@AgNPs-4MBA that bound at T-line decreased and the intensity of the Raman signal at T-line became weaker. The Raman signal intensity at T-line decreased, as the concentration of Cd2+ in the samples increased. Exposure times of the Raman spectrometer were maintained at 20 s. The results for detecting different concentrations of Cd2+ are shown in Fig. 3b–c. When negative samples were applied to the ICSs, the Raman signal intensity at T-line reached 2300 a.u. The SERS signal intensity began decreasing when Cd2+ concentrations were greater than 0.05 ng/mL, and SERS signal intensity gradually decreased when Cd2+ concentrations increased. When Cd2+ concentrations were higher than 25 ng/mL, the signal at T-line remained at approximately 100 a.u. As shown in Fig. 3c, the calibration curve of SERS ICSs for detecting Cd2+ shows a negative slope and a linear detection range between 0.05 and 25 ng/mL. The LOD of SERS ICSs was 0.05 ng/mL, which was calculated by concentration response to the SERS intensity (SERS intensity of negative sample – 3 × SD). A thermal accelerated test was used to study the storage time of SERS ICSs for detecting Cd2+ ion. These SERS ICSs were stored at 37 °C and SERS intensity of the ICSs was kept constant for 30 days. According to Arrhenius equation, the developed SERS ICSs could be stored for 120 days at 25 °C (Additional file 1: Figure S43).

Fig. 3
figure 3

a Schematic diagram of the SERS ICSs for detecting Cd2+. b Concentration dependent SERS spectra of the ICSs obtained from the precipitates that corresponded to different concentrations of Cd2+. The entire SERS spectra are shown in Additional file 1: Figure S24–38. c Calibration curve of SERS ICSs for the detection of Cd2+

Comparison of SERS ICSs and AuNPs ICSs for detecting haemoglobin and Cd2+

A comparison of SERS ICSs and AuNPs ICSs based on the same antigen and antibody is shown in Table 1. The sensitivity of SERS ICSs is higher than AuNPs ICSs and has a wider dynamic detection range.

Table 1 Comparison of SERS ICSs, AuNPs ICSs

Specificity of the SERS ICSs

The cross reactivity of SERS ICSs is shown in Fig. 4. For studying specificity of SERS ICSs that detect haemoglobin, 20,000 ng/mL of thrombin, casein, BSA, and OVA were dissolved in PBS and then detected using the SERS ICSs. The results indicated that the SERS ICSs had low cross reactivity with casein, BSA, and OVA. While researching the specificity of SERS ICSs used to detect Cd2+, various metal ions (25 ng/mL) were spiked in water samples and then detected by using SERS ICSs. The results indicated that the developed ICSs had cross-reaction rates of 0.55, 0.02, 2.24, 1.32, 0.89, 0.38, 0.30, 0.36, 0.85, 0.87, 0, and 1.28 % with Co2+, Cu2+, Fe2+, Hg2+, K+, Li+, Mg2+, Na+, Ni+, Pb2+, Zn2+, and Al3+ respectively. These results indicated that the developed SERS ICSs had high specificity.

Fig. 4
figure 4

Specificity of the SERS ICSs. a Specificity of the SERS ICSs for detecting hemoglobin. b Specificity of the SERS ICSs for detecting Cd2+

Recovery of SERS ICSs for detecting haemoglobin and Cd2+

While studying the recovery of SERS ICSs for detecting haemoglobin, SERS ICSs were also used to detect haemoglobin that had been spiked in blood and stool samples. Additionally, while researching the recovery of SERS ICSs for detecting Cd2+, SERS ICSs were used to detect Cd2+ that were spiked in tap water, river water, and soil leaching water. Table 2 summarizes the recovery of SERS ICSs. Recoveries of SERS ICSs that detected haemoglobin spiked in serum and stool varied from 5.06 to 14.8 %. For detecting Cd2+ spiked in tap water, Pearl River water, and soil leaching water, the recoveries of SERS ICSs were ranged from 90.67 to 110.0 %, 96.0 to 120.0 % and 92.00 to 116 %, respectively. These correlated results that haemoglobin was detected by using ELISA and Cd2+ was detected by using ICP-MASS.

Table 2 Recovery of SERS ICSs for detecting haemoglobin and Cd2+

Conclusion

In conclusion, because of their core–shell structures and rough surfaces, RSAu@AgNPs have a high Raman enhancement efficiency, and be used to fabricate high sensitivity SERS ICSs for detecting haemoglobin and Cd2+. When compared with AuNPs ICSs, the developed SERS ICSs possessed a higher sensitivity, which indicated that SERS ICSs could detect lower concentrations of analytes when AuNPs ICSs were unavailable. In actual testing, pH, ionic strengths, and impurities in samples often affected the stability and accuracy of detection results. Therefore, by using SERS ICSs, samples could be diluted many times to reduce the effects of pH, ionic strength, and impurities. These results indicate that SERS ICSs are ideal tools for clinical diagnoses, food safety testing, and environmental pollution monitoring.

References

  1. Abe K, Nakamura K, Arao T, Sakurai Y, Nakano A, Suginuma C, Tawarada K, Sasaki K. Immunochromatography for the rapid determination of cadmium concentrations in wheat grain and eggplant. J Sci Food Agric. 2011;91:1392–7.

    Article  CAS  Google Scholar 

  2. Fang Z, Wu W, Lu X, Zeng L. Lateral flow biosensor for DNA extraction-free detection of salmonella based on aptamer mediated strand displacement amplification. Biosens Bioelectron. 2014;56:192–7.

    Article  CAS  Google Scholar 

  3. Fu Q, Liang J, Lan C, Zhou K, Shi C, Tang Y. Development of a novel dual-functional lateral-flow sensor for on-site detection of small molecule analytes. Sensors Actuators B Chem. 2014;203:683–9.

    Article  CAS  Google Scholar 

  4. Fu Q, Tang Y, Shi C, Zhang X, Xiang J, Liu X. A novel fluorescence-quenching immunochromatographic sensor for detection of the heavy metal chromium. Biosens Bioelectron. 2013;49:399–402.

    Article  CAS  Google Scholar 

  5. Oh YK, Joung H-A, Han HS, Suk H-J, Kim M-G. A three-line lateral flow assay strip for the measurement of C-reactive protein covering a broad physiological concentration range in human sera. Biosens Bioelectron. 2014;61:285–9.

    Article  CAS  Google Scholar 

  6. Liu X, Xiang J-J, Tang Y, Zhang X-L, Fu Q-Q, Zou J-H, Lin Y. Colloidal gold nanoparticle probe-based immunochromatographic assay for the rapid detection of chromium ions in water and serum samples. Anal Chim Acta. 2012;745:99–105.

    Article  CAS  Google Scholar 

  7. Lönnberg M, Carlsson J. Quantitative detection in the attomole range for immunochromatographic tests by means of a flatbed scanner. Anal Biochem. 2001;293:224–31.

    Article  Google Scholar 

  8. Khreich N, Lamourette P, Boutal H, Devilliers K, Créminon C, Volland H. Detection of Staphylococcus enterotoxin B using fluorescent immunoliposomes as label for immunochromatographic testing. Anal Biochem. 2008;377:182–8.

    Article  CAS  Google Scholar 

  9. Khreich N, Lamourette P, Lagoutte B, Ronco C, Franck X, Créminon C, Volland H. A fluorescent immunochromatographic test using immunoliposomes for detecting microcystins and nodularins. Anal Bioanal Chem. 2010;397:1733–42.

    Article  CAS  Google Scholar 

  10. Zou Z, Du D, Wang J, Smith JN, Timchalk C, Li Y, Lin Y. Quantum dot-based immunochromatographic fluorescent biosensor for biomonitoring trichloropyridinol, a biomarker of exposure to chlorpyrifos. Anal Chem. 2010;82:5125–33.

    Article  CAS  Google Scholar 

  11. Yang Q, Gong X, Song T, Yang J, Zhu S, Li Y, Cui Y, Li Y, Zhang B, Chang J. Quantum dot-based immunochromatography test strip for rapid, quantitative and sensitive detection of alpha fetoprotein. Biosens Bioelectron. 2011;30:145–50.

    Article  CAS  Google Scholar 

  12. Wen L, Zhu P, Liu Y, Pan Q, Qu Y, Xu X, Li X, Fu N. Development of a fluorescence immunochromatographic assay for the detection of zeta globin in the blood of (− − SEA) α-thalassemia carriers. Blood Cells Mol Dis. 2012;49:128–32.

    Article  CAS  Google Scholar 

  13. Oh SW, Kim YM, Kim HJ, Kim SJ, Cho J-S, Choi EY. Point-of-care fluorescence immunoassay for prostate specific antigen. Clin Chim Acta. 2009;406:18–22.

    Article  CAS  Google Scholar 

  14. Bian X, Song Z-L, Qian Y, Gao W, Cheng Z-Q, Chen L, Liang H, Ding D, Nie X-K, Chen Z. Fabrication of graphene-isolated-Au-nanocrystal nanostructures for multimodal cell imaging and photothermal-enhanced chemotherapy. Sci Rep. 2014; 4.

  15. Song Z-L, Chen Z, Bian X, Zhou L-Y, Ding D, Liang H, Zou Y-X, Wang S-S, Chen L, Yang C. Alkyne-functionalized superstable graphitic silver nanoparticles for Raman imaging. J Am Chem Soc. 2014;136:13558–61.

    Article  CAS  Google Scholar 

  16. Narayanan N, Karunakaran V, Paul W, Venugopal K, Sujathan K, Maiti KK. Aggregation induced Raman scattering of squaraine dye: implementation in diagnosis of cervical cancer dysplasia by SERS imaging. Biosens Bioelectron. 2015;70:145–52.

    Article  CAS  Google Scholar 

  17. Kang H, Jeong S, Park Y, Yim J, Jun BH, Kyeong S, Yang JK, Kim G, Hong S, Lee LP. Near-infrared SERS nanoprobes with plasmonic Au/Ag hollow-shell assemblies for in vivo multiplex detection. Adv Funct Mater. 2013;23:3719–27.

    Article  CAS  Google Scholar 

  18. Kircher MF, de la Zerda A, Jokerst JV, Zavaleta CL, Kempen PJ, Mittra E, Pitter K, Huang R, Campos C, Habte F. A brain tumor molecular imaging strategy using a new triple-modality MRI-photoacoustic-Raman nanoparticle. Nat Med. 2012;18:829–34.

    Article  CAS  Google Scholar 

  19. Qian X, Peng X-H, Ansari DO, Yin-Goen Q, Chen GZ, Shin DM, Yang L, Young AN, Wang MD, Nie S. In vivo tumor targeting and spectroscopic detection with surface-enhanced Raman nanoparticle tags. Nat Biotechnol. 2008;26:83–90.

    Article  CAS  Google Scholar 

  20. Moore BD, Stevenson L, Watt A, Flitsch S, Turner NJ, Cassidy C, Graham D. Rapid and ultra-sensitive determination of enzyme activities using surface-enhanced resonance Raman scattering. Nat Biotechnol. 2004;22:1133–8.

    Article  CAS  Google Scholar 

  21. Hu PP, Liu H, Zhen SJ, Li CM, Huang CZ. Nanosilver-based surface-enhanced Raman spectroscopic determination of DNA methyltransferase activity through real-time hybridization chain reaction. Biosens Bioelectron. 2015;73:228–33.

    Article  CAS  Google Scholar 

  22. Cao YC, Jin R, Mirkin CA. Nanoparticles with Raman spectroscopic fingerprints for DNA and RNA detection. Science. 2002;297:1536–40.

    Article  CAS  Google Scholar 

  23. Faulds K, Smith WE, Graham D. Evaluation of surface-enhanced resonance Raman scattering for quantitative DNA analysis. Anal Chem. 2004;76:412–7.

    Article  CAS  Google Scholar 

  24. Lo H-C, Hsiung H-I, Chattopadhyay S, Han H-C, Chen C-F, Leu JP, Chen K-H, Chen L-C. Label free sub-picomole level DNA detection with Ag nanoparticle decorated Au nanotip arrays as surface enhanced Raman spectroscopy platform. Biosens Bioelectron. 2011;26:2413–8.

    Article  CAS  Google Scholar 

  25. Mahajan S, Richardson J, Brown T, Bartlett PN. SERS-melting: a new method for discriminating mutations in DNA sequences. J Am Chem Soc. 2008;130:15589–601.

    Article  CAS  Google Scholar 

  26. Chen Z, Tabakman SM, Goodwin AP, Kattah MG, Daranciang D, Wang X, Zhang G, Li X, Liu Z, Utz PJ. Protein microarrays with carbon nanotubes as multicolor Raman labels. Nat Biotechnol. 2008;26:1285–92.

    Article  CAS  Google Scholar 

  27. Wu L, Wang Z, Zong S, Huang Z, Zhang P, Cui Y. A SERS-based immunoassay with highly increased sensitivity using gold/silver core-shell nanorods. Biosens Bioelectron. 2012;38:94–9.

    Article  CAS  Google Scholar 

  28. Chung E, Gao R, Ko J, Choi N, Lim DW, Lee EK, Chang S-I, Choo J. Trace analysis of mercury (ii) ions using aptamer-modified Au/Ag core–shell nanoparticles and SERS spectroscopy in a microdroplet channel. Lab Chip. 2013;13:260–6.

    Article  CAS  Google Scholar 

  29. Kim NH, Lee SJ, Moskovits M. Aptamer-mediated surface-enhanced Raman spectroscopy intensity amplification. Nano Lett. 2010;10:4181–5.

    Article  CAS  Google Scholar 

  30. Fang Y, Seong N-H, Dlott DD. Measurement of the distribution of site enhancements in surface-enhanced Raman scattering. Science. 2008;321:388–92.

    Article  CAS  Google Scholar 

  31. Le Ru E, Etchegoin P. Phenomenological local field enhancement factor distributions around electromagnetic hot spots. J Chem Phys. 2009;130:181101.

    Article  Google Scholar 

  32. Frosch T, Meyer T, Schmitt M, Popp J. Device for Raman difference spectroscopy. Anal Chem. 2007;79:6159–66.

    Article  CAS  Google Scholar 

  33. Pile D. Raman spectroscopy: phone sensing. Nat Photonics. 2014;8:168.

    Google Scholar 

  34. Rong H, Liu A, Jones R, Cohen O, Hak D, Nicolaescu R, Fang A, Paniccia M. An all-silicon Raman laser. Nature. 2005;433:292–4.

    Article  CAS  Google Scholar 

  35. Rong H, Xu S, Kuo Y-H, Sih V, Cohen O, Raday O, Paniccia M. Low-threshold continuous-wave Raman silicon laser. Nat Photonics. 2007;1:232–7.

    Article  CAS  Google Scholar 

  36. Li JF, Huang YF, Ding Y, Yang ZL, Li SB, Zhou XS, Fan FR, Zhang W, Zhou ZY, Ren B. Shell-isolated nanoparticle-enhanced Raman spectroscopy. Nature. 2010;464:392–5.

    Article  CAS  Google Scholar 

  37. Lim D-K, Jeon K-S, Hwang J-H, Kim H, Kwon S, Suh YD, Nam J-M. Highly uniform and reproducible surface-enhanced Raman scattering from DNA-tailorable nanoparticles with 1-nm interior gap. Nat Nanotechnol. 2011;6:452–60.

    Article  CAS  Google Scholar 

  38. Liu W, Zhu Z, Deng K, Li Z, Zhou Y, Qu H, Gao Y, Che S, Tang Z. Gold nanorod@chiral mesoporous silica core-shell nanoparticles with unique optical properties. J Am Chem Soc. 2013;135:9659–64.

    Article  CAS  Google Scholar 

  39. Zhu Z, Meng H, Liu W, Liu X, Gong J, Qiu X, Jiang L, Wang D, Tang Z. Superstructures and SERS properties of gold nanocrystals with different shapes. Angew Chem Int Ed. 2011;50:1593–6.

    Article  CAS  Google Scholar 

  40. Han B, Zhu ZN, Li ZT, Zhang W, Tang ZY. Conformation Modulated Optical Activity Enhancement In Chiral Cysteine and Au nanorod assemblies. J Am Chem Soc. 2014;136:16104–7.

    Article  CAS  Google Scholar 

  41. Samal AK, Polavarapu L, Rodal-Cedeira S, Liz-Marzan LM, Perez-Juste J, Pastoriza-Santos I. Size tunable Au@Ag core shell nanoparticles: synthesis and surface-enhanced Raman scattering properties. Langmuir. 2013;29:15076–82.

    Article  CAS  Google Scholar 

  42. Xie J, Zhang Q, Lee JY, Wang DI. The synthesis of SERS-active gold nanoflower tags for in vivo applications. ACS Nano. 2008;2:2473–80.

    Article  CAS  Google Scholar 

  43. Tian ZQ, Ren B, Wu DY. Surface-enhanced Raman scattering: from noble to transition metals and from rough surfaces to ordered nanostructures. J Phys Chem B. 2002;106:9463–83.

    Article  CAS  Google Scholar 

  44. Chantarawong W, Takeda K, Sangartit W, Yoshizawa M, Pradermwong K, Shibahara S. Microphthalmia-associated transcription factor as the molecular target of cadmium toxicity in human melanocytes. Biochem Biophys Res Commun. 2014;454:594–9.

    Article  CAS  Google Scholar 

  45. Vergauwen L, Hagenaars A, Blust R, Knapen D. Temperature dependence of long-term cadmium toxicity in the zebrafish is not explained by liver oxidative stress: evidence from transcript expression to physiology. Aquat Toxicol. 2013;126:52–62.

    Article  CAS  Google Scholar 

Download references

Authors’ contributions

QF carried out prepration of the SERS ICSs and drafted the manuscript; HL carried out detect Cd and hemoglobin by using SERS ICSs; ZW carried out preparation of AuPlISA for detecting Cd2+ and hemoglobin; AL carried out operation of Raman spectrometer; CY and XL carried out preparation of AuNPs and Au@AgNPs; SY and WX carried out operation of ELISA for detecting Cd2+ and hemoglobin; ZL carried raise the ideas and provide some instruments; YT carried raise raise the ideas, provide funding and drafted the manuscript. All authors read and approved the final manuscript.

Acknowledgements

This work was supported by the Technology Research Program of Guangzhou City (201508020100), the Technology Research Program of Guangdong Province (2013B0104104027), the Introduction Program for Innovative Entrepreneurial Team of Guangdong Province (201301S0105240297) and the National Science Foundation of China (Grant No. 11204105). We offer our appreciation to Charron Cote for helping with English revisions for this manuscript.

Competing interests

The authors declare that they have no competing interests.

Author information

Authors and Affiliations

Authors

Corresponding authors

Correspondence to Zhi Luo or Yong Tang.

Additional information

Qiangqiang Fu and Hongwu Liu contributed equally to the manuscript

Additional file

Rights and permissions

Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Fu, Q., Liu, H.L., Wu, Z. et al. Rough surface Au@Ag core–shell nanoparticles to fabricating high sensitivity SERS immunochromatographic sensors. J Nanobiotechnol 13, 81 (2015). https://doi.org/10.1186/s12951-015-0142-0

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/s12951-015-0142-0

Keywords